Tailoring the corrosion resistance of Zn-Mn coating by electrodeposition from deep eutectic solvents / Poboljšanje korozione postojanosti Zn-Mn prevlake, elektrohemijskim taloženjem iz dubokih eutektičkih smeša
(Belgrade, Serbia : Engineering Society for Corrosion, 2018)
Well adhered, homogenous coatings were obtained from deep eutectic solvents (DES) based on choline chloride and urea, at current densities up to 20 mA cm-2. The coatings' morphology was analyzed by atomic force microscopy, ...
The resistance to general corrosion of series of zinc-aluminum alloys modified with silicon and strontiumloys modified with silicon and strontium / Otpornost na opštu koroziju serije legura cink-aluminijum koje su modifikovane silicijumom i stroncijumom
(Belgrade : Engineering Society for Corrosion, 2019)
The resistance to corrosion of the series of zinc-aluminum casting alloys modified with silicon and
strontium was studied in a sodium chloride solution. It was shown that general corrosion was the
main form of corrosion ...
Testing the protective ability of corrosion inhibitors in dilute chloride solutions / Ispitivanje zaštitne sposobnosti inhibitora korozije u razblaženim rastvorima hlorida
(Belgrade, Serbia : Engineering Society for Corrosion, 2017)
After sterilization of meat cans in a factory of meat and meat products in Serbia, occurence of corrosion on the can lids was observed. Sterilization of cans is usually performed in the presence of corrosion inhibitors. ...
Determination of the weld metal corrosion rate using electrochemical techniques / Određivanje brzine korozije metala šava u zavarenom spoju pomoću elektrohemijskih tehnika
(Belgrade, Serbia : Engineering Society for Corrosion, 2015)
To determine corrosion rate of the base metal and weld metal were applied electrochemical techniques: linear polarization resistance, linear sweep voltammetry and electrochemical impedance spectroscopy. The samples were ...
Chemical corrosion of metals and alloys / Hemijska korozija metala i legura
(Belgrade, Serbia : Engineering Society for Corrosion, 2016)
In this paper, phenomena of chemical corrosion of metals and alloys in electrolyte solutions are analyzed. It is shown that iron, chromium and other metals and alloys dissolve much faster than is the corrosion rate determined ...
Influence of welding current intensity on pitting corrosion resistance in welded joint of stainless steel X5CrNi18-10 / Uticaj jačine struje zavarivanja na otpornost prema piting koroziji zavarenog spoja nerđajućeg čelika X5CrNi18-10
(Belgrade, Serbia : Engineering Society for Corrosion, 2017)
The effect of welding current on the pitting corrosion resistance in the welded joint of austenitic stainless steel X5CrNi18-10 was tested. Welding was carried out using three different current intensity (110 A, 130 A and ...
Water quality as one of the possible causative agents of corrosion in thermal power plants / Kvalitet vode kao jedan od mogućih uzročnika korozije u termoenergetskim postrojenjima
(Belgrade, Serbia : Engineering Society for Corrosion, 2010)
Damage and cancellations of thermal power plants in large numbers are caused due to an inadequate quality of feed water, which occur due to different types of corrosion processes. Water is a good solvent and its chemical ...
Correlation between crystal orientation and morphology of electrolytically produced powder particles: Analysis of the limiting cases / Korelacija izmedju orijentacije kristala i morfologije elektrolitički proizvedenih praškastih čestica - analiza graničnih slučajeva
(Belgrade, Serbia : Engineering Society for Corrosion, 2018)
Lead and nickel powder particles were produced by the processes of electrolysis and characterized by scanning electron microscope (SEM). The X-ray diffraction (XRD) analysis of the produced particles was done. Morphologies ...
Morphology of Fe-Ni alloy powders electrodeposited from citrate-sulfate containing solutions / Morfologija prahova Fe-Ni legura elektrohemijski istaloženih iz citratno-sulfatnih rastvora
(Belgrade, Serbia : Engineering Society for Corrosion, 2011)
The electrochemical deposition of the Fe-Ni alloy powders from citrate-sulfate containing electrolytes of different Ni/Fe ions concentration ratios at pH 4.5 was examined by the polarization measurements. All polarization ...
Influence of the synthesis procedures on pt catalyst activity for ethanol electrooxidation reaction / Uticaj postupka sinteze na aktivnost platinskih katalizatora za reakciju elektrooksidacije etanola
(Belgrade, Serbia : Engineering Society for Corrosion, 2016)
Carbon supported platinum catalysts for ethanol electrooxidation were synthesized by modified polyol synthesis method, assisted by microwave or reflux heating. Synthesized catalysts were characterized by XRD, STM and TGA ...