Macroporous monoliths based оn natural mineral sources, clay аnd diatomite
(Belgrade : Association for ETRAN Society, 2020)
Macroporous silica ceramic was obtained using clay and diatomite. Boric acid as a low-cost additive in the amount of 1 wt% was used. These porous materials were obtained at low forming pressure (40-80 MPa) and lower sintering ...
Effect оf delamination оn physico-chemical properties оf kaolin
(International Institute for the Science of Sintering (IISS), 2021)
To provide the quality required for its use, raw kaolin must be subjected to certain processing procedures like delamination which is applied to the layered structure materials. The aim of this research is to determine the ...
The Influence of pH on Electrochemical Behavior of Nicotine- Clay based Electrodes
(Belgrade : International Institute for the Science of Sintering (IISS), 2021)
Montmorillonite based clay was acid activated. Nicotine was adsorbed on untreated
and acid activated clay from its aqueous solution at either pH=6 or pH=9.26 (unadjusted pH
solution). The XRD analysis revealed that the ...
Impact of Alumina Particles on the Morphology and Mechanics of Hybrid Wood Plastic Composite Materials
(Belgrade : Association for ETRAN Society, 2019)
Hybrid composite panels of Wood-Plastic Composites (WPC) consisting of wood and
poly (methyl methacrylate) (PMMA) were reinforced with alumina particles and made by
“hot pressing” method. Alumina-based particles were ...
Co supported chitosan-derived carbon-smectite catalyst in Oxone® induced at dye degradation
(Serbian Ceramic Society, 2023)
Catalytic degradation of tartrazine in the presence of Oxone® activated by a catalyst constituted of cobalt supported on a nanocomposite of smectite with chitosan-derived carbon was investigated. The catalyst was synthesized ...
One-Pot Combustion Synthesis of Nickel Oxide and Hematite: from Simple Coordination Compounds to High Purity Metal Oxide Nanoparticles
(Belgrade : International Institute for the Science of Sintering, 2020)
This work is the first report of a very simple and fast one-pot synthesis of nickel oxide (NiO) and hematite (α-Fe2O3) nanoparticles by thermal decomposition of transition metal aqua complexes with camphor sulfonate anions. ...
Understanding the Effect of Synthesis and Sintering Temperature on the Functional Properties of Barium Titanate/ Cobalt Ferrite Composites
(Association for ETRAN Society, 2023)
To investigate the effect of synthesis procedure and sintering temperature on the functional properties of perovskite/spinel ceramics, BaTiO3/CoFe2O4 composites were prepared by thermal decomposition, coprecipitation, and ...
Evaluation of adsorption performance and quantum chemical modeling of pesticides removal using cell-MG hybrid adsorbent
(Belgrade : International Institute for the Science of Sintering (IISS), 2021)
Magnetite (MG) modified cellulose membrane (Cell-MG), obtained by reaction of 3-aminosilane and subsequently with diethylenetriaminepentaacetic acid dianhydride functionalized waste Cell fibers (Cell-NH2 and Cell-DTPA, ...
Oxide Powder Mixture with Poly-vinyl Alcohol (PVA) and added Polyethylene Glycol (PEG) as Plasticizer
(Belgrade : Association for ETRAN Society, 2023)
Powder mixture consisted of ZnO, Mn2O3 (MnCO3) and Fe2O3 blended powders, was found laminating during compaction. Polyvinyl alcohol (PVA) and a combination of PVA with polyethylene glycol (PEG) added as a plasticizer, were ...
Multiferroic Heterostructure BaTiO3/ε-Fe2O3 Composite Obtained by in situ Reaction
(Belgrade : International Institute for the Science of Sintering, 2021)
Solid-state reaction between BaTiO3 and Fe2O3 was used to produce a multiferroic heterostructure composite. Commercial BaTiO3 and Fe(NO3)3•9H2O were suspended in ethanol for 30 minutes in an ultrasound bath. The prepared ...