Morphology and internal structure of copper deposits electrodeposited by the pulsating current regime in the hydrogen co-deposition range
(Springer, New York, 2012)
The effect of the regime of pulsating current (PC) on copper electrodeposition in the hydrogen co-deposition range was examined by the techniques of scanning electron and optical microscopes. The quantities of evolved ...
Application of pulsating overpotential regime on the formation of copper deposits in the range of hydrogen co-deposition
(Springer, New York, 2010)
Electrodeposition of copper by pulsating overpotential (PO) regime in the range of hydrogen co-deposition was examined by scanning electron microscopy. It was found that the increase of the pause-to-pulse ratio produced a ...
Protective ability and impedance response of sol-gel reversely transformed ceria conversion coating on aluminium
(Springer, New York, 2016)
Ceria coating is formed on Al from the ceria sol prepared exclusively by forced hydrolysis of Ce(NO3)(4), in order to test their ability to protect Al from corrosion. The characterization of sol-gel-processed ceria coating ...
Formation of two-dimensional (2D) lead dendrites by application of different regimes of electrolysis
(Springer, New York, 2012)
Electrodeposition of lead from nitrate electrolyte in constant regimes of electrolysis was analyzed and the obtained powder lead deposits were examined by scanning electron microscopy. Polarization curve for lead ...
The electrochemical behavior of PtRu- and Pt-modified zeolite X in alkaline solution
(Springer, New York, 2013)
Zeolite NaX was modified by Pt and Pt/Ru nanodispersed metallic clusters. The procedure of impregnation with acetylacetonate salt/acetone solution was applied. Scanning electron microscope analysis confirmed partial zeolite ...
Electrochemical behavior of silver-impregnated Al-pillared smectite in alkaline solution
(Springer, New York, 2010)
In order to enhance silver effectiveness for oxygen reduction reaction, pillared clay was used as a support for silver nanodispersion. Silver particles incorporation into pillared clay pores was attempted by impregnation/thermal ...
Oxygen reduction reaction on palladium-modified zeolite 13X
(Springer, New York, 2015)
Palladium was dispersed over zeolite NaX by procedure of impregnation/thermal degradation of palladium acetylacetonate salt. Samples characterization was performed by X-ray diffraction, SEM analysis, and chemical analysis. ...
Microwave-assisted polyol synthesis of carbon-supported platinum-based bimetallic catalysts for ethanol oxidation
(Springer, New York, 2012)
High surface area carbon-supported Pt, PtRh, and PtSn catalysts were synthesized by microwave-assisted polyol procedure and tested for ethanol oxidation in perchloric acid. The catalysts were characterized by thermogravimetric ...
Insight into electrocatalytic stability of low loading Pt-Bi/GC and Pt/GC clusters in formic acid oxidation
(Springer, New York, 2015)
Formic acid oxidation was examined on platinum-bismuth deposits on glassy carbon substrate prepared by two-step process, i.e., electrochemical deposition of Bi followed by electrochemical deposition of Pt as described in ...
Oxidation of carbon monoxide and formic acid on bulk and nanosized Pt-Co alloys
(Springer, New York, 2012)
Bulk Pt3Co and nanosized Pt3Co and PtCo alloys supported on high area carbon were investigated as the electrocatalysts for the COads and HCOOH oxidation. Pt3Co alloy with Co electrochemically leached from the surface (Pt ...