Electrochemical and structural properties of Ni(II)-alumina composites as an annealing temperature function
(International Institute for the Science of Sintering, Beograd, 2019)
Alumina powders, pure and doped with nickel, were synthetized by sol-gel method and calcined at 500, 900 and 1100°C in order to obtain mesoporous structures with a high specific surface area, well adapTab. to catalytic ...
Structural characterization of the nickel thin film deposited by glad technique
(International Institute for the Science of Sintering, Beograd, 2013)
In this work, a columnar structure of nickel thin film has been obtained using an advanced deposition technique known as Glancing Angle Deposition. Nickel thin film was deposited on glass sample at the constant emission ...
Thermal diffusivity of single crystal Bi0.9Sb0.1
(International Institute for the Science of Sintering, Beograd, 2010)
A single crystal Bi0.9Sb0.1 ingot was synthesized using the Bridgman technique. Thermal diffusivity and electronic transport properties of single crystal cleaved plates (00l) were determined from PA photoacoustic phase and ...
ZnTiO3 ceramic nanopowder microstructure changes during compaction
(International Institute for the Science of Sintering, Beograd, 2013)
ZnTiO3 nanopowder as a constitutive component in compact production was primarily characterized. Scanning electron micrographs of as received powder were recorded. Mercury porosimetry and nitrogen adsorption were also ...
Synthesis of Highly Porous Al2O3-YAG Composite Ceramics
(International Institute for the Science of Sintering, Beograd, 2016)
Al2O3-YAG composite was obtained by sintering of porous Al2O3 preforms infiltrated with water solution of aluminium nitrate nonahydrate, Al(NO3)(3)center dot 9H(2)O and yttrium nitrate hexahydrate, Y(NO3)(3)center dot ...
Ecologically Friendly Chitosan-montmorillonite Bio-nanocomposite as Adsorbent for Textile Dyes from Aqueous Solutions
(International Institute for the Science of Sintering, Beograd, 2017)
The bio-nanocomposite of montmorillonite and natural biopolymer chitosan (C-MM) was synthesized. Intercalation of chitosan in form of monolayer into the interlamellar space of montmorillonite was confirmed by XRD and IR ...
Cyclic Voltammetric Study of the Influence of Porosity on Electrochemical Response of Nickel-Alumina Modified Glassy Carbon Electrode
(International Institute for the Science of Sintering, Beograd, 2018)
Pure and nickel-modified alumina powders with different porosity were synthesized and applied on the glassy carbon electrode by means of Nafion polymer. The data obtained from the nitrogen adsorption-desorption isotherm ...
Methanol electrooxidation on PtRu modified zeolite X
(International Institute for the Science of Sintering, Beograd, 2013)
Zeolite NaX (faujasite type) was used as a support for platinum-ruthenium catalyst. A procedure for thermal decomposition of noble metal acetylacetonates to deposit noble metal clusters on the surface of solid support was ...
Formation of Magnetic Microstructure of the Nanosized NiFe2O4 Synthesized Via Solid-State Reaction
(International Institute for the Science of Sintering, Beograd, 2012)
Magnetic NiFe2O4 structure formation was studied through structural, compositional and magnetic characterization of obtained reaction products of a simple, high yielding and low-cost solid-state reaction. Initial annealing ...
Microstructure refinement and physical properties of Ag-SnO2 based contact materials prepared by high-energy ball milling
(International Institute for the Science of Sintering, Beograd, 2013)
High energy ball milling was used in order to improve dispersion of metal oxide in Ag-SnO2 electrical contact materials. The processed Ag-SnO2 (92:8) and Ag-SnO2In2O3 (87.8:9.30:2.9) powder mixtures were subsequently ...