Microwave-assisted polyol synthesis of carbon-supported platinum-based bimetallic catalysts for ethanol oxidation
(Springer, New York, 2012)
High surface area carbon-supported Pt, PtRh, and PtSn catalysts were synthesized by microwave-assisted polyol procedure and tested for ethanol oxidation in perchloric acid. The catalysts were characterized by thermogravimetric ...
Oxidation of carbon monoxide and formic acid on bulk and nanosized Pt-Co alloys
(Springer, New York, 2012)
Bulk Pt3Co and nanosized Pt3Co and PtCo alloys supported on high area carbon were investigated as the electrocatalysts for the COads and HCOOH oxidation. Pt3Co alloy with Co electrochemically leached from the surface (Pt ...
Oxygen reduction reaction on palladium-modified zeolite 13X
(Springer, New York, 2015)
Palladium was dispersed over zeolite NaX by procedure of impregnation/thermal degradation of palladium acetylacetonate salt. Samples characterization was performed by X-ray diffraction, SEM analysis, and chemical analysis. ...
The electrochemical behavior of PtRu- and Pt-modified zeolite X in alkaline solution
(Springer, New York, 2013)
Zeolite NaX was modified by Pt and Pt/Ru nanodispersed metallic clusters. The procedure of impregnation with acetylacetonate salt/acetone solution was applied. Scanning electron microscope analysis confirmed partial zeolite ...
Electrochemical behavior of silver-impregnated Al-pillared smectite in alkaline solution
(Springer, New York, 2010)
In order to enhance silver effectiveness for oxygen reduction reaction, pillared clay was used as a support for silver nanodispersion. Silver particles incorporation into pillared clay pores was attempted by impregnation/thermal ...
Titanium coated with high-performance nanocrystalline ruthenium oxide synthesized by the microwave-assisted sol-gel procedure
(Springer, New York, 2016)
Ruthenium oxide coating on titanium was prepared by the sol-gel procedure from well-defined colloidal oxide dispersions synthesized by the microwave (MW)-assisted hydrothermal route under defined temperature and pressure ...
Insight into electrocatalytic stability of low loading Pt-Bi/GC and Pt/GC clusters in formic acid oxidation
(Springer, New York, 2015)
Formic acid oxidation was examined on platinum-bismuth deposits on glassy carbon substrate prepared by two-step process, i.e., electrochemical deposition of Bi followed by electrochemical deposition of Pt as described in ...
Pt/C nanocatalysts for methanol electrooxidation prepared by water-in-oil microemulsion method
(Springer, New York, 2016)
Pt nanoparticles supported on Vulcan XC-72R were synthesized by water-in-oil microemulsion method. By incorporating different amounts of HCl as a capping agent in the precursor-containing water phase, nanoparticle shape ...
Electrodeposited Pd and PdNi coatings as electrodes for the electrochemical oxidation of ethanol in alkaline media
(Springer, New York, 2017)
Electrodeposition of Pd and PdNi coating samples of different thicknesses, depending on the coating composition and current efficiency, was achieved galvanostatically on the rotating Au disc electrode from the plating bath ...
Pd black decorated by Pt sub-monolayers as an electrocatalyst for the HCOOH oxidation
(Springer, New York, 2014)
Pd black was modified by a very low amount of Pt corresponding to a sub-monolayer (ML). Spontaneous displacement method was employed. The catalysts with 0.02-0.12 ML were characterized by cyclic voltammetry and COads ...