Influence of welding current intensity on susceptibility to intergranular corrosion in welded joints of stainless steel / Uticaj jačine struje zavarivanja na sklonost prema interkristalnoj koroziji zavarenog spoja nerdajućeg čelika
(DUZS - Društvo za unapređivanje zavarivanja u Srbiji, Beograd, 2017)
Susceptibility to intergranular corrosion in welded joints of austenitic stainless steel X5Cr-Ni18-10 was tested. The welding was performed with different intensity of welding current (110 A, 130 A and 150 A). The tests ...
Testing of susceptibility to intergranular corrosion in welded joints of austenitic stainless steel / Određivanje sklonosti zavarenog spoja austenitnog nerđajućeg čelika prema interkristalnoj koroziji
(DUZS - Društvo za unapređivanje zavarivanja u Srbiji, Beograd, 2016)
The susceptibility to intergranular corrosion of welded joints of austenitic stainless steel X5CrNi18-10 was examined. The testing was performed by the electrochemical potentiokinetic reactivation method with single loop ...
Pitting corrosion testing of stainless steel AISI 304 in chloride solutions / Ispitivanje piting korozije nerđajućeg čelika AISI 304 u rastvorima hlorida
(DUZS - Društvo za unapređivanje zavarivanja u Srbiji, Beograd, 2015)
Stainless steels and their welded joints are often susceptible to pitting corrosion in solutions containing chloride ions. Testing of pitting corrosion of stainless steels is performed using chemical and electrochemical ...
Preventing and removing of heat tint / Sprečavanje i uklanjanje termičkog oksida (heat tint)
(DUZS - Društvo za unapređivanje zavarivanja u Srbiji, Beograd, 2014)
Heat tinting is a thickening of the naturally occurring oxide layer on the surface of the stainless steels during welding. The thickness of the oxide layer next to the weld depends on the temperature, heating time, and ...