The effect of perpendicularly oriented magnetic field on the formation of very disperse iron structures / Uticaj vertikalno orijentisanog magnetnog polja na formiranje veoma disperznih struktura gvožđa
(Serbian Chemical Society, 2006)
Iron deposits obtained without and with a perpendicularly oriented magnetic field were examined by scanning electron microscopy (SEM). It was found that the iron deposit obtained under a perpendicularly oriented magnetic ...
The effects of a magnetic field on the morphologies of nickel and copper deposits: The concept of 'effective overpotential' / Uticaj primenjenih magnetnih polja na morfologije taloga nikla i bakra - koncept 'efektivne prenapetosti'
(Serbian Chemical Society, 2007)
The morphologies of nickel and copper deposits obtained without applied magnetic fields, and with both parallel and perpendicular applied magnetic fields were examined by the scanning electron microscopy (SEM) technique. ...
Effect of temperature on the electrodeposition of disperse copper deposits / Uticaj temperature na elektrohemijsko taloženje disperznih taloga bakra
(Serbian Chemical Society, 2007)
The effect of temperature on the electrodeposition of copper at overpotentials belonging to the plateau of the limiting diffusion current density and higher was examined by the determination of the average current efficiency ...
Some aspects of nickel electrodeposition in the presence of a magnetic field / Neki aspekti taloženja nikla u prisustvu magnetnog polja
(Serbian Chemical Society, 2005)
Nickel deposits obtained from a Watt solution both without and with a perpendicularly oriented magnetic field were examined by scanning electron microscopy (SEM). The nickel deposit obtained without an imposed magnetic ...
Cross-section analysis of the morphology of electrodeposited copper obtained in the hydrogen co-deposition range / Morfologija poprečnog preseka prevlaka bakra dobijenih elektrohemijskim taloženjem u oblasti ko-depozicije vodonika
(Serbian Chemical Society, 2009)
Cross-section analysis of copper deposits electrodeposited in the hydrogen co-deposition range at a constant overpotential and in a pulsating overpotential (PO) regime was performed. It was shown that a complete structural ...