Nanostructural Analysis of Mirror – Bright Zinc Coatings
(MAIK "Nauka /Interperiodica" (Russia), 2006)
The zinc coatings electrode posited from solution containing dextrin/salicyl aldehyde mixture are
examined by the scanning tunneling microscopy (STM). It is shown that mirror brightness of these zinc deposits is associated ...
The effects of the pause to pulse ratio in the regime of pulsating overpotential on the formation of honeycomb-like structures
(Elsevier Science Inc, New York, 2009)
The formation of honeycomb-like structures in the pulsating overpotential (PO) regime was examined by scanning electron microscopy (SEM). The honeycomb-like structures obtained with a square-wave PO of different pause to ...
Structural characteristics of bright copper surfaces
(Journal of Electroanalytical Chemistry, 2001)
In this work, the structures of copper surfaces polished mechanically and polished both mechanically and electrochemically, as well as copper coatings obtained in the presence of basic and top brightening addition agents ...
Influence of potential pulse conditions on the formation of honeycomb-like copper electrodes
(Elsevier, 2009)
Electrodeposition of copper by pulsating overpotential (PO) regime in the hydrogen co-deposition range was examined by the determination of the average current efficiency of hydrogen evolution and by microscopic analysis ...
Electrochemical deposition and characterization of Zn /Co alloys and corrosion protection by electrodeposited epoxy coating on Zn /Co alloy
(Elsevier, 2002)
Zn-Co alloys electrochemically deposited on steel under various deposition conditions were investigated. The influence of deposition current density, temperature and composition of deposition solution on the phase structure ...
The Preferred Orientation of Bright Copper Deposits
(Switzerland : Trans Tech Publications Ltd, 2000)
The preferred orientations of copper deposits obtained from acid sulfate solutions were examined. Mat deposits obtained in the absence of the additives and in the presence of disodium 2-naphtol-3,6-disulfonic acid possessed ...
Electrodeposition of Ni, Co and Ni–Co alloy powders
(Elsevier, 2006)
In this paper the polarization characteristics of the processes of Ni and Co powders and Ni-Co alloy powders electrodeposition from ammonium sulfate containing supporting electrolyte are investigated as a function of Ni ...
Ballistic magnetoresistance versus magnetostriction effects in electrodeposited nanocontacts at room temperature
(Institute of Electrical and Electronics Engineers, Inc., 2003)
The authors present experiments and discuss recent results on ballistic magnetotesistance in nanometer size (on the order of 1 to 10 nm) nanocontacts grown by electrodeposition in
thin wires and in thin films of a few ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...