Ecologically Friendly Chitosan-montmorillonite Bio-nanocomposite as Adsorbent for Textile Dyes from Aqueous Solutions
(International Institute for the Science of Sintering, Beograd, 2017)
The bio-nanocomposite of montmorillonite and natural biopolymer chitosan (C-MM) was synthesized. Intercalation of chitosan in form of monolayer into the interlamellar space of montmorillonite was confirmed by XRD and IR ...
Thermal diffusivity of single crystal Bi0.9Sb0.1
(International Institute for the Science of Sintering, Beograd, 2010)
A single crystal Bi0.9Sb0.1 ingot was synthesized using the Bridgman technique. Thermal diffusivity and electronic transport properties of single crystal cleaved plates (00l) were determined from PA photoacoustic phase and ...
Magnetic properties of ND Rich Melt-Spun ND-FE-B alloy
(International Institute for the Science of Sintering, Beograd, 2005)
As a part of these experimental investigations of melt-spun Nd-Fe-B alloy with Nd rich content in relation to Nd2Fe14B prepared by rapid quenching process for optimally selected cooling rate and heat treatment, the influence ...
Investigation of the conditions of synthesis composite optical fiber-magnetic powder
(Sintering Society, 2000)
The goal of these investigations was synthesis of composite optical fiber-magnetic powder with new application possibilities like sensors, detectors etc. The part of results of investigation of the possibility of embedding ...
The influence of protective atmosphere on oxidation of sintered SmCo5 magnetic materials
(ETRAN Society, 1996)
Understanding of the thermal stability of intermetallic SmCo5 powder is essential for designing the working atmosphere in all phases of the technological procedure in the production of sintered SmCo5 magnets to obtain ...
Macroporous monoliths based оn natural mineral sources, clay аnd diatomite
(Belgrade : Association for ETRAN Society, 2020)
Macroporous silica ceramic was obtained using clay and diatomite. Boric acid as a low-cost additive in the amount of 1 wt% was used. These porous materials were obtained at low forming pressure (40-80 MPa) and lower sintering ...
Synthesis of Highly Porous Al2O3-YAG Composite Ceramics
(International Institute for the Science of Sintering, Beograd, 2016)
Al2O3-YAG composite was obtained by sintering of porous Al2O3 preforms infiltrated with water solution of aluminium nitrate nonahydrate, Al(NO3)(3)center dot 9H(2)O and yttrium nitrate hexahydrate, Y(NO3)(3)center dot ...
ZnTiO3 ceramic nanopowder microstructure changes during compaction
(International Institute for the Science of Sintering, Beograd, 2013)
ZnTiO3 nanopowder as a constitutive component in compact production was primarily characterized. Scanning electron micrographs of as received powder were recorded. Mercury porosimetry and nitrogen adsorption were also ...
Cyclic Voltammetric Study of the Influence of Porosity on Electrochemical Response of Nickel-Alumina Modified Glassy Carbon Electrode
(International Institute for the Science of Sintering, Beograd, 2018)
Pure and nickel-modified alumina powders with different porosity were synthesized and applied on the glassy carbon electrode by means of Nafion polymer. The data obtained from the nitrogen adsorption-desorption isotherm ...
Two Step Sintering of ZnTiO3 nanopowder
(International Institute for the Science of Sintering, Beograd, 2017)
Metastable nanopowder ZnTiO3 was pressed into cylindrical compacts at 200 MPa. Compacts were treated by conventional heating with isothermal holding at 931 degrees C for 10 minutes, 25 minutes and 40 minutes. ZnTiO3 compacts ...