Structural characterization of the nickel thin film deposited by glad technique
(International Institute for the Science of Sintering, Beograd, 2013)
In this work, a columnar structure of nickel thin film has been obtained using an advanced deposition technique known as Glancing Angle Deposition. Nickel thin film was deposited on glass sample at the constant emission ...
Electrochemical and structural properties of Ni(II)-alumina composites as an annealing temperature function
(International Institute for the Science of Sintering, Beograd, 2019)
Alumina powders, pure and doped with nickel, were synthetized by sol-gel method and calcined at 500, 900 and 1100°C in order to obtain mesoporous structures with a high specific surface area, well adapTab. to catalytic ...
Synthesis of Highly Porous Al2O3-YAG Composite Ceramics
(International Institute for the Science of Sintering, Beograd, 2016)
Al2O3-YAG composite was obtained by sintering of porous Al2O3 preforms infiltrated with water solution of aluminium nitrate nonahydrate, Al(NO3)(3)center dot 9H(2)O and yttrium nitrate hexahydrate, Y(NO3)(3)center dot ...
Impact of Alumina Particles on the Morphology and Mechanics of Hybrid Wood Plastic Composite Materials
(Belgrade : Association for ETRAN Society, 2019)
Hybrid composite panels of Wood-Plastic Composites (WPC) consisting of wood and
poly (methyl methacrylate) (PMMA) were reinforced with alumina particles and made by
“hot pressing” method. Alumina-based particles were ...
Ecologically Friendly Chitosan-montmorillonite Bio-nanocomposite as Adsorbent for Textile Dyes from Aqueous Solutions
(International Institute for the Science of Sintering, Beograd, 2017)
The bio-nanocomposite of montmorillonite and natural biopolymer chitosan (C-MM) was synthesized. Intercalation of chitosan in form of monolayer into the interlamellar space of montmorillonite was confirmed by XRD and IR ...
Two Step Sintering of ZnTiO3 nanopowder
(International Institute for the Science of Sintering, Beograd, 2017)
Metastable nanopowder ZnTiO3 was pressed into cylindrical compacts at 200 MPa. Compacts were treated by conventional heating with isothermal holding at 931 degrees C for 10 minutes, 25 minutes and 40 minutes. ZnTiO3 compacts ...
Methanol electrooxidation on PtRu modified zeolite X
(International Institute for the Science of Sintering, Beograd, 2013)
Zeolite NaX (faujasite type) was used as a support for platinum-ruthenium catalyst. A procedure for thermal decomposition of noble metal acetylacetonates to deposit noble metal clusters on the surface of solid support was ...
Cyclic Voltammetric Study of the Influence of Porosity on Electrochemical Response of Nickel-Alumina Modified Glassy Carbon Electrode
(International Institute for the Science of Sintering, Beograd, 2018)
Pure and nickel-modified alumina powders with different porosity were synthesized and applied on the glassy carbon electrode by means of Nafion polymer. The data obtained from the nitrogen adsorption-desorption isotherm ...
The Effect of Sintering Temperature on Mesoporous Structure of WO3 Doped Tio(2) Powders
(International Institute for the Science of Sintering, Beograd, 2018)
In this study, WO3 doped TiO2 powders were synthesized via sol-gel method combined with a hydrothermal process. The effect of sintering temperature on mesoporous structure and catalytic activities of these powders were ...
Formation of Magnetic Microstructure of the Nanosized NiFe2O4 Synthesized Via Solid-State Reaction
(International Institute for the Science of Sintering, Beograd, 2012)
Magnetic NiFe2O4 structure formation was studied through structural, compositional and magnetic characterization of obtained reaction products of a simple, high yielding and low-cost solid-state reaction. Initial annealing ...