Superior photocatalytic properties of carbonized PANI/TiO2 nanocomposites
Аутори
Radoicic, MarijaCiric-Marjanovic, Gordana
Spasojevic, Vuk
Ahrenkiel, Scott Phillip
Mitrić, Miodrag
Novaković, Tatjana
Šaponjić, Zoran
Чланак у часопису (Рецензирана верзија)
Метаподаци
Приказ свих података о документуАпстракт
A simple bottom-up method for the preparation of novel and very efficient photocatalytic nanocomposite system based on carbonized form of polyaniline (PANI) and colloidal TiO2 nanocrystals has been developed. The carbonized PANI/TiO2 nanocomposites were synthesized in a two-step procedure. Firstly, non-carbonized PANI/TiO2 nanocomposites were synthesized by the chemical oxidative polymerization of aniline (ANI) with ammonium peroxydisulfate, in the presence of colloidal TiO2 nanoparticles (TiO2 NPs) (d 4.5 nm). Initial [TiO2 NANI] mole ratios were 20, 50, and 80. In the second step, following the polymerization process, the carbonization of PANI/TiO2 nanocomposites was performed by thermal treatment in an inert atmosphere at 650 degrees C. The morphological and structural properties of the carbonized nanocomposites were studied using transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray powder diffraction (XRD) and Raman spectroscopy. The accomplishment of c...omplete carbonization of PANI in PANI/TiO2 nanocomposites was confirmed by Raman spectroscopy. The appearance of anatase and rutile crystal forms in TiO2 NPs upon carbonization, with mass ratio depending on the initial molar ratio of ANI and TiO2 NPs was revealed by XRD measurements, TEM, SEM and Raman spectroscopy. The photocatalytic activities of carbonized PANI/TiO2 nanocomposites were evaluated following the photocatalytic degradation processes of Rhodamine B and Methylene blue. Carbonized PANI/TiO2 nanocomposites showed higher photocatalytic efficacy compared to bare TiO2 NPs and non-carbonized PANI/TiO2 nanocomposites. The porosity and surface structure of carbonized PANI/TiO2 nanocomposites, as well as crystalline structure of TiO2, affect photocatalytic activity of nanocomposites.
Кључне речи:
Photocatalysis / TiO2 / Carbonized polyanilineИзвор:
Applied Catalysis B-Environmental, 2017, 213, 155-166Издавач:
- Elsevier
Финансирање / пројекти:
- Утицај величине, облика и структуре наночестица на њихова својства и својства нанокомпозита (RS-MESTD-Basic Research (BR or ON)-172056)
- Електропроводни и редокс-активни полимери и олигомери: синтеза, структура, својства и примена (RS-MESTD-Basic Research (BR or ON)-172043)
- Материјали редуковане димензионалности за ефикасну апсорпцију светлости и конверзију енергије (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45020)
Напомена:
- This is peer-reviewed version of the article: Marija Radoicic, Gordana Ciric-Marjanovic, Vuk Spasojevic, Phil Ahrenkiel, Miodrag Mitric, Tatjana Novakovic, Zoran Saponjic, Superior photocatalytic properties of carbonized PANI/TiO2 nanocomposites, Applied Catalysis B-Environmental, 2017, 213, 155-166 https://dx.doi.org/10.1016/j.apcatb.2017.05.023
- http://cer.ihtm.bg.ac.rs/handle/123456789/2238
DOI: 10.1016/j.apcatb.2017.05.023
ISSN: 0926-3373
WoS: 000402633300016
Scopus: 2-s2.0-85018897251
Институција/група
IHTMTY - JOUR AU - Radoicic, Marija AU - Ciric-Marjanovic, Gordana AU - Spasojevic, Vuk AU - Ahrenkiel, Scott Phillip AU - Mitrić, Miodrag AU - Novaković, Tatjana AU - Šaponjić, Zoran PY - 2017 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/3018 AB - A simple bottom-up method for the preparation of novel and very efficient photocatalytic nanocomposite system based on carbonized form of polyaniline (PANI) and colloidal TiO2 nanocrystals has been developed. The carbonized PANI/TiO2 nanocomposites were synthesized in a two-step procedure. Firstly, non-carbonized PANI/TiO2 nanocomposites were synthesized by the chemical oxidative polymerization of aniline (ANI) with ammonium peroxydisulfate, in the presence of colloidal TiO2 nanoparticles (TiO2 NPs) (d 4.5 nm). Initial [TiO2 NANI] mole ratios were 20, 50, and 80. In the second step, following the polymerization process, the carbonization of PANI/TiO2 nanocomposites was performed by thermal treatment in an inert atmosphere at 650 degrees C. The morphological and structural properties of the carbonized nanocomposites were studied using transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray powder diffraction (XRD) and Raman spectroscopy. The accomplishment of complete carbonization of PANI in PANI/TiO2 nanocomposites was confirmed by Raman spectroscopy. The appearance of anatase and rutile crystal forms in TiO2 NPs upon carbonization, with mass ratio depending on the initial molar ratio of ANI and TiO2 NPs was revealed by XRD measurements, TEM, SEM and Raman spectroscopy. The photocatalytic activities of carbonized PANI/TiO2 nanocomposites were evaluated following the photocatalytic degradation processes of Rhodamine B and Methylene blue. Carbonized PANI/TiO2 nanocomposites showed higher photocatalytic efficacy compared to bare TiO2 NPs and non-carbonized PANI/TiO2 nanocomposites. The porosity and surface structure of carbonized PANI/TiO2 nanocomposites, as well as crystalline structure of TiO2, affect photocatalytic activity of nanocomposites. PB - Elsevier T2 - Applied Catalysis B-Environmental T1 - Superior photocatalytic properties of carbonized PANI/TiO2 nanocomposites VL - 213 SP - 155 EP - 166 DO - 10.1016/j.apcatb.2017.05.023 ER -
@article{ author = "Radoicic, Marija and Ciric-Marjanovic, Gordana and Spasojevic, Vuk and Ahrenkiel, Scott Phillip and Mitrić, Miodrag and Novaković, Tatjana and Šaponjić, Zoran", year = "2017", abstract = "A simple bottom-up method for the preparation of novel and very efficient photocatalytic nanocomposite system based on carbonized form of polyaniline (PANI) and colloidal TiO2 nanocrystals has been developed. The carbonized PANI/TiO2 nanocomposites were synthesized in a two-step procedure. Firstly, non-carbonized PANI/TiO2 nanocomposites were synthesized by the chemical oxidative polymerization of aniline (ANI) with ammonium peroxydisulfate, in the presence of colloidal TiO2 nanoparticles (TiO2 NPs) (d 4.5 nm). Initial [TiO2 NANI] mole ratios were 20, 50, and 80. In the second step, following the polymerization process, the carbonization of PANI/TiO2 nanocomposites was performed by thermal treatment in an inert atmosphere at 650 degrees C. The morphological and structural properties of the carbonized nanocomposites were studied using transmission electron microscopy (TEM), scanning electron microscopy (SEM), X-ray powder diffraction (XRD) and Raman spectroscopy. The accomplishment of complete carbonization of PANI in PANI/TiO2 nanocomposites was confirmed by Raman spectroscopy. The appearance of anatase and rutile crystal forms in TiO2 NPs upon carbonization, with mass ratio depending on the initial molar ratio of ANI and TiO2 NPs was revealed by XRD measurements, TEM, SEM and Raman spectroscopy. The photocatalytic activities of carbonized PANI/TiO2 nanocomposites were evaluated following the photocatalytic degradation processes of Rhodamine B and Methylene blue. Carbonized PANI/TiO2 nanocomposites showed higher photocatalytic efficacy compared to bare TiO2 NPs and non-carbonized PANI/TiO2 nanocomposites. The porosity and surface structure of carbonized PANI/TiO2 nanocomposites, as well as crystalline structure of TiO2, affect photocatalytic activity of nanocomposites.", publisher = "Elsevier", journal = "Applied Catalysis B-Environmental", title = "Superior photocatalytic properties of carbonized PANI/TiO2 nanocomposites", volume = "213", pages = "155-166", doi = "10.1016/j.apcatb.2017.05.023" }
Radoicic, M., Ciric-Marjanovic, G., Spasojevic, V., Ahrenkiel, S. P., Mitrić, M., Novaković, T.,& Šaponjić, Z.. (2017). Superior photocatalytic properties of carbonized PANI/TiO2 nanocomposites. in Applied Catalysis B-Environmental Elsevier., 213, 155-166. https://doi.org/10.1016/j.apcatb.2017.05.023
Radoicic M, Ciric-Marjanovic G, Spasojevic V, Ahrenkiel SP, Mitrić M, Novaković T, Šaponjić Z. Superior photocatalytic properties of carbonized PANI/TiO2 nanocomposites. in Applied Catalysis B-Environmental. 2017;213:155-166. doi:10.1016/j.apcatb.2017.05.023 .
Radoicic, Marija, Ciric-Marjanovic, Gordana, Spasojevic, Vuk, Ahrenkiel, Scott Phillip, Mitrić, Miodrag, Novaković, Tatjana, Šaponjić, Zoran, "Superior photocatalytic properties of carbonized PANI/TiO2 nanocomposites" in Applied Catalysis B-Environmental, 213 (2017):155-166, https://doi.org/10.1016/j.apcatb.2017.05.023 . .