Structural characterization and electrical properties of sintered magnesium-titanate ceramics
Само за регистроване кориснике
2013
Аутори
Filipović, SuzanaObradovic, Nina
Krstić, Jugoslav
Scepanovic, M.
Pavlović, Vladimir B.
Paunović, Vesna
Ristic, M. M.
Чланак у часопису (Објављена верзија)
Метаподаци
Приказ свих података о документуАпстракт
In this article the influence of ball miling process on structure of MgO-TiO2 system, as well as the electrical properties of samples after sintering, was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 min. The influence of mechanical activation and sintering on the lattice vibrational spectra was studied by Raman spectroscopy at room temperature. Structural investigations have been performed on produced powders. Nitrogen adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results have been obtained: specific surface area continuosly decreased up to 40 min of activation and increased after that, reaching its minimun value of 5.5 m(2)/g. The Raman spectra of activated powders have shown that anatase modes have been decreasing in intensity and broadening as the time of activation extended. Also, the additional modes attributed to TiO2 II, srilankite... and rutile phases started to appear as a consequence of activation. The small differences noticed in the Raman spectra of sintered samples have been explained by structural modification of MgTiO3 phase due to the presence of defects. The effects of activation and sintering process on microstructure were investigated by scanning electron microscopy (SEM). The electrical measurements showed difference in dielectric constant (epsilon(r)), loss tangent (tg delta) and specific resistance (rho) as a function of time of mechanical treatment.
Кључне речи:
Ball milling / SEM / Raman spectroscopy / Sintering / TitanatesИзвор:
Journal of Alloys and Compounds, 2013, 555, 39-44Издавач:
- Elsevier
Финансирање / пројекти:
- Усмерена синтеза, структура и својства мултифункционалних материјала (RS-MESTD-Basic Research (BR or ON)-172057)
DOI: 10.1016/j.jallcom.2012.12.040
ISSN: 0925-8388
WoS: 000314909700008
Scopus: 2-s2.0-84871898069
Институција/група
IHTMTY - JOUR AU - Filipović, Suzana AU - Obradovic, Nina AU - Krstić, Jugoslav AU - Scepanovic, M. AU - Pavlović, Vladimir B. AU - Paunović, Vesna AU - Ristic, M. M. PY - 2013 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/1274 AB - In this article the influence of ball miling process on structure of MgO-TiO2 system, as well as the electrical properties of samples after sintering, was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 min. The influence of mechanical activation and sintering on the lattice vibrational spectra was studied by Raman spectroscopy at room temperature. Structural investigations have been performed on produced powders. Nitrogen adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results have been obtained: specific surface area continuosly decreased up to 40 min of activation and increased after that, reaching its minimun value of 5.5 m(2)/g. The Raman spectra of activated powders have shown that anatase modes have been decreasing in intensity and broadening as the time of activation extended. Also, the additional modes attributed to TiO2 II, srilankite and rutile phases started to appear as a consequence of activation. The small differences noticed in the Raman spectra of sintered samples have been explained by structural modification of MgTiO3 phase due to the presence of defects. The effects of activation and sintering process on microstructure were investigated by scanning electron microscopy (SEM). The electrical measurements showed difference in dielectric constant (epsilon(r)), loss tangent (tg delta) and specific resistance (rho) as a function of time of mechanical treatment. PB - Elsevier T2 - Journal of Alloys and Compounds T1 - Structural characterization and electrical properties of sintered magnesium-titanate ceramics VL - 555 SP - 39 EP - 44 DO - 10.1016/j.jallcom.2012.12.040 ER -
@article{ author = "Filipović, Suzana and Obradovic, Nina and Krstić, Jugoslav and Scepanovic, M. and Pavlović, Vladimir B. and Paunović, Vesna and Ristic, M. M.", year = "2013", abstract = "In this article the influence of ball miling process on structure of MgO-TiO2 system, as well as the electrical properties of samples after sintering, was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 min. The influence of mechanical activation and sintering on the lattice vibrational spectra was studied by Raman spectroscopy at room temperature. Structural investigations have been performed on produced powders. Nitrogen adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results have been obtained: specific surface area continuosly decreased up to 40 min of activation and increased after that, reaching its minimun value of 5.5 m(2)/g. The Raman spectra of activated powders have shown that anatase modes have been decreasing in intensity and broadening as the time of activation extended. Also, the additional modes attributed to TiO2 II, srilankite and rutile phases started to appear as a consequence of activation. The small differences noticed in the Raman spectra of sintered samples have been explained by structural modification of MgTiO3 phase due to the presence of defects. The effects of activation and sintering process on microstructure were investigated by scanning electron microscopy (SEM). The electrical measurements showed difference in dielectric constant (epsilon(r)), loss tangent (tg delta) and specific resistance (rho) as a function of time of mechanical treatment.", publisher = "Elsevier", journal = "Journal of Alloys and Compounds", title = "Structural characterization and electrical properties of sintered magnesium-titanate ceramics", volume = "555", pages = "39-44", doi = "10.1016/j.jallcom.2012.12.040" }
Filipović, S., Obradovic, N., Krstić, J., Scepanovic, M., Pavlović, V. B., Paunović, V.,& Ristic, M. M.. (2013). Structural characterization and electrical properties of sintered magnesium-titanate ceramics. in Journal of Alloys and Compounds Elsevier., 555, 39-44. https://doi.org/10.1016/j.jallcom.2012.12.040
Filipović S, Obradovic N, Krstić J, Scepanovic M, Pavlović VB, Paunović V, Ristic MM. Structural characterization and electrical properties of sintered magnesium-titanate ceramics. in Journal of Alloys and Compounds. 2013;555:39-44. doi:10.1016/j.jallcom.2012.12.040 .
Filipović, Suzana, Obradovic, Nina, Krstić, Jugoslav, Scepanovic, M., Pavlović, Vladimir B., Paunović, Vesna, Ristic, M. M., "Structural characterization and electrical properties of sintered magnesium-titanate ceramics" in Journal of Alloys and Compounds, 555 (2013):39-44, https://doi.org/10.1016/j.jallcom.2012.12.040 . .