Electrochemical synthesis and corrosion behavior of polyaniline-benzoate coating on copper
Само за регистроване кориснике
АуториGvozdenović, Milica M.
Grgur, Branimir N.
Jugovic, Zvonimir S.
Чланак у часопису (Објављена верзија)
МетаподациПриказ свих података о документу
Electrochemical polymerization of polyaniline (PANI) coating on copper electrode was performed galvanostatically in the current density range between 0.50 and 1.25 mA cm(-2), from aqueous solution of 0.3 mol dm(-3) sodium benzoate and 0.2 mol dm(-3) aniline. The corrosion behavior of PANI coated copper and copper electrode exposed to 0.5 mol dm(-3) sodium chloride solution was investigated by potentiodynamic and electrochemical impedance spectroscopy techniques. It was observed that thin PANI (5 mu m) coating had provided efficient protection (similar to 96%) to copper in 0.5 mol dm(-3) sodium chloride solution. Unusual initial impedance behavior to that normally observed with conventional organic coatings was attributed to dedoping of benzoate anions from the polymer coating.
Кључне речи:Electrochemical polymerization / Sodium benzoate / Polyaniline / Copper
Извор:Synthetic Metals, 2011, 161, 13-14, 1313-1318
- Elsevier Science Sa, Lausanne