Micromorphological and chemical changes on the glazed ceramics irradiated by the CO2 laser

Abstract

This paper presents the results of the micromorphological and chemical changes on the surface of a glazed ceramic sample irradiated by the CO2 laser. The tested sample is a part of a title. The laser irradiation effects were studied as a function of the number of laser pulses and lase fluences around and over the damage threshold. The obtained modifications were investigated because these are essential in laser processing of the ceramics. The CO2 laser with λ= 10.6 μm and full width at half the maximum pulse τ=100 ps has been used for the surface treatment. The ceramic surface morphology modifications, induced by laser, were characterized by a scanning electron microscope (SEM), while the composition was examined by energy-dispersive (EDX) and X-ray fluorescence (XRF) spectroscopy. The results show that there are significant differences depending on the applied laser fluences and number of pulses.

У раду су приказани резултати испитивања микроморфолошких и хемијских промена на површини глазиране керамике, озрачене CO2 ласером. Испитивани узорак је део керамичке плочице. Ефекти ласерског деловања су испитивани у зависности од броја ласерских импулса и ласерске флуенце око и изнад прага пштећења. Добијене промене су испитиване јер су веома значајне у ласерској обради керамике. CO2 ласер са таласном дужином λ= 10.6 μm и трајањем импулса τ=100 ps, је коришћен за обраду површине. Морфолошке промене површине керамике изазване деловањем ласером су испитане скенирајућим електронсим микроскопом (СЕМ), а хемијски састав испитан је EDX и X-ray флуоресцентном спектроскопијом (XRF). Резултати показују да постоје значајне разлике у зависности од примењених ласерских флуенци и броја импулса.