Anticorrosion activity of 2-thiоhуdantoin–Shiff base derivatives for mild steel in 0.5 M HCl

Abstract

Several 2-thiohydаntоin–Shiff base derivatives were prepared as ecofriendly corrosion inhibitors for mild steel in acid environment. Their anticorrosion properties were studied on mild steel in 0.5 M HCl solution as corrosion electrolyte by using usuаl grаvimеtriс and different elесtrосhemicаl techniques (wеight lоss mеаsurеmеnt, pоtеntiоdynаmiс pоlаrizаtiоn and pоtеntiоstаtiс еlесtrосhеmicаl impеdаnсе sресtrоscору). Mild steel surface was characterized using two analytical techniques, scanning electron microscopy for surface morphology and elemental composition and atomic force microscopy. The study has shown that the inhibiting action of these environmentally benign inhibitors synthesized from inexpensive commercially available starting materials could be attributed to adsorption on the metal surface.

Неколико деривата Шифових база 2-тиохидантоина су направљени као еколошки прихватљиви инхибитори корозије меког челика у киселој средини. Њихова антикорозиона својства су испитана на меком челику у 0,5 M раствору HCl као корозионом електролиту, користећи уобичајене гравиметријске и различите електрохемијске технике (мерење губитка масе, потенциодинамичка поларизација, потенциостатска спектроскопија електрохемијске импеданције). Површина меког челика је окарактерисана двема аналитичким техникама, скенирајућом електронском микроскопијом за морфологију површине и елементарни састав и микроскопијом атомске силе. Студија је показала да се инхибиторно деловање ових еколошки бенигних инхибитора, синтетисаних из јефтиних комерцијално доступних полазних материјала, може приписати адсорпцији инхибитора на површини меког челика.