Cerium citrate as ecologically friendly corrosion inhibitor for AA7075 alloy
Abstract
The corrosion behaviour of high-strength AA7075 aluminium alloy in NaCl solution, without and in the presence of environmentally friendly corrosion inhibitors (Ce-chloride and Ce-citrate) in low concentrations ( lt 0.5 mM), was analysed. The degree of precipitation of the solid solution of AA7075 alloy was determined by measuring the electrical conductivity, while the surface morphology and appearance of intermetallic compounds before and after corrosion testing were analysed by SEM/EDS method. The general corrosion resistance of the tested alloy in NaCl solution and the degree of the inhibitory effect of the corrosion inhibitors were determined on the basis of electrochemical impedance spectroscopy and polarization measurements, while resistance to pit formation on the bases of E-pit. AA7075 alloy showed high resistance to general corrosion in the presence of both tested inhibitors, while resistance to pit formation was significantly higher in the presence of Ce-citrate (concentratio...n 0.5 mM). Also, Ce-citrate present in NaCl solution at lower concentrations provides satisfactory resistance of AA7075 alloy to general and pitting corrosion. A mechanism of protective action of Ce-citrate inhibitor has been proposed.
Keywords:
aluminium alloy / Ce-citrate / corrosion inhibitors / EIS / SEM / EDSSource:
Materials and Corrosion-Werkstoffe Und Korrosion, 2022, 73, 950-960Publisher:
- Wiley
Funding / projects:
- Ministry of Education, Science and Technological Development, Republic of Serbia, Grant no. 200026 (University of Belgrade, Institute of Chemistry, Technology and Metallurgy - IChTM) (RS-200026)
- Ministry of Education, Science and Technological Development, Republic of Serbia, Grant no. 200135 (University of Belgrade, Faculty of Technology and Metallurgy) (RS-200135)
DOI: 10.1002/maco.202112900
ISSN: 0947-5117
WoS: 000745085000001
Scopus: 2-s2.0-85123254780
Collections
Institution/Community
IHTMTY - JOUR AU - Marunkić, Dunja AU - Pejić, Jovanka AU - Jegdić, Bore AU - Marinković, Aleksandar AU - Radojković, Bojana PY - 2022 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/5251 AB - The corrosion behaviour of high-strength AA7075 aluminium alloy in NaCl solution, without and in the presence of environmentally friendly corrosion inhibitors (Ce-chloride and Ce-citrate) in low concentrations ( lt 0.5 mM), was analysed. The degree of precipitation of the solid solution of AA7075 alloy was determined by measuring the electrical conductivity, while the surface morphology and appearance of intermetallic compounds before and after corrosion testing were analysed by SEM/EDS method. The general corrosion resistance of the tested alloy in NaCl solution and the degree of the inhibitory effect of the corrosion inhibitors were determined on the basis of electrochemical impedance spectroscopy and polarization measurements, while resistance to pit formation on the bases of E-pit. AA7075 alloy showed high resistance to general corrosion in the presence of both tested inhibitors, while resistance to pit formation was significantly higher in the presence of Ce-citrate (concentration 0.5 mM). Also, Ce-citrate present in NaCl solution at lower concentrations provides satisfactory resistance of AA7075 alloy to general and pitting corrosion. A mechanism of protective action of Ce-citrate inhibitor has been proposed. PB - Wiley T2 - Materials and Corrosion-Werkstoffe Und Korrosion T1 - Cerium citrate as ecologically friendly corrosion inhibitor for AA7075 alloy VL - 73 SP - 950 EP - 960 DO - 10.1002/maco.202112900 ER -
@article{ author = "Marunkić, Dunja and Pejić, Jovanka and Jegdić, Bore and Marinković, Aleksandar and Radojković, Bojana", year = "2022", abstract = "The corrosion behaviour of high-strength AA7075 aluminium alloy in NaCl solution, without and in the presence of environmentally friendly corrosion inhibitors (Ce-chloride and Ce-citrate) in low concentrations ( lt 0.5 mM), was analysed. The degree of precipitation of the solid solution of AA7075 alloy was determined by measuring the electrical conductivity, while the surface morphology and appearance of intermetallic compounds before and after corrosion testing were analysed by SEM/EDS method. The general corrosion resistance of the tested alloy in NaCl solution and the degree of the inhibitory effect of the corrosion inhibitors were determined on the basis of electrochemical impedance spectroscopy and polarization measurements, while resistance to pit formation on the bases of E-pit. AA7075 alloy showed high resistance to general corrosion in the presence of both tested inhibitors, while resistance to pit formation was significantly higher in the presence of Ce-citrate (concentration 0.5 mM). Also, Ce-citrate present in NaCl solution at lower concentrations provides satisfactory resistance of AA7075 alloy to general and pitting corrosion. A mechanism of protective action of Ce-citrate inhibitor has been proposed.", publisher = "Wiley", journal = "Materials and Corrosion-Werkstoffe Und Korrosion", title = "Cerium citrate as ecologically friendly corrosion inhibitor for AA7075 alloy", volume = "73", pages = "950-960", doi = "10.1002/maco.202112900" }
Marunkić, D., Pejić, J., Jegdić, B., Marinković, A.,& Radojković, B.. (2022). Cerium citrate as ecologically friendly corrosion inhibitor for AA7075 alloy. in Materials and Corrosion-Werkstoffe Und Korrosion Wiley., 73, 950-960. https://doi.org/10.1002/maco.202112900
Marunkić D, Pejić J, Jegdić B, Marinković A, Radojković B. Cerium citrate as ecologically friendly corrosion inhibitor for AA7075 alloy. in Materials and Corrosion-Werkstoffe Und Korrosion. 2022;73:950-960. doi:10.1002/maco.202112900 .
Marunkić, Dunja, Pejić, Jovanka, Jegdić, Bore, Marinković, Aleksandar, Radojković, Bojana, "Cerium citrate as ecologically friendly corrosion inhibitor for AA7075 alloy" in Materials and Corrosion-Werkstoffe Und Korrosion, 73 (2022):950-960, https://doi.org/10.1002/maco.202112900 . .