Refractive index increments of di‐n‐alkylitaconate polymers and copolymers

Abstract

Refractive index increments of 11 poly(di‐n‐alkylitaconate) polymers were determined systematically in seven organic solvents, expected to be suitable for light scattering and other solution property measurements. Of 13 solvents tried, poly(dimethylitaconate) was soluble only in 6, however higher members of the polymer series exhibit better solubility. The measured dn/dc values in butanone and ethyl‐and amylacetate are practically independent of an increase of the number of carbon atoms in the ester substituents of the monomer, however a decrease of the values for solvents with higher refractive indices can be observed. For statistical poly(styrene‐co‐di‐n‐alkylitaconate) samples the additive character of dn/dc in butanone and toluene was observed and verified from copolymer compositions determined by UV and elemental analysis.

Brechungsinkremente von elf verschiedenen Di-n-alkylitakonat-Polymerewn urden systematisch in sieben organischen Losungsmitteln bestimmt, um eine giinstige Auswahl fiir Lichtstreuungs- und andere Losung~igenschaftsmessungeznu ermoglichen. Polydimethylitakonat war nur in sechs von 13 untersuchten Losungsmitteln loslich, wiihrend hohere Glieder der Polymerenreihe bedeutend bessere Loslichkeiten aufwiesen. Die ermittelten dn/dc Werte in Butanon, Athyl- und Amylacetat hangen praktisch von einer Zunahme der Zahl der Kohlenstoffatome in den Estersubstituenten nicht ab; bei Losungsmitteln mit hoheren Brechungsindizes ist aber eine sinkende Tendenz der Werte bemerkbar. Bei statistischen Copolymeren aus Styrol und Di-n-alkylitakonat wird der additive Charakter von dn/dc in Butanon und Toluol bemerkbar, welcher durch Bestimmung der chemischen Zusammensetzung mittels UV und Kohlenstoffgehalt bestiitigt werden konnte.