Preparation and modification of itaconic anhydride-methyl methacrylate copolymers

Abstract

The free radical copolymerisation of itaconic anhydride and methyl methacrylate in solution was studied at 60°C. The copolymer composition was determined by 1H-NMR spectroscopy and the obtained monomer reactivity ratios were calculated, rITA = 1.35±0.11; rMMA = 0.22±0.22 (by the Fineman-Ross method) and rITA = 1.27±0.38; rMMA = 0.10±0.05 (by the Mayo-Lewis method). The synthesised copolymers were modified by reaction with di-n-butyl amine. The copolymer composition after amidation was determined by elemental analysis via the nitrogen content. Amidation of the anhydride units in the copolymers with di-n-butyl amine resulted in complete conversion to itaconamic acid.

Испитивана је радикална кополимеризација анхидрида итаконске киселине и метил-метакрилата у раствору на 60 °C. Састав кополимера одређен је 1H-NMR спектроскопијом и израчунати су односи реактивности мономера, rITA = 1.35±0.11; rMMA = 0.22±0.22 (методом Фајнман–Рос) и rITA = 1.27±0.38; rMMA = 0.10±0.05 (методом Мејо–Луис). Синтетизовани кополимери су модификовани реакцијом са дибутиламином. Након амидације састав кополимера одређен је елементалном анализом на основу садржаја азота. Амидацијом анхидридних јединица у кополимерима дибутил-амином настале су комономерне јединице итаконамичне киселине.