dc.description.abstractThe influence of the chemical composition on the biosorption potential of waste jute fabric for Ni2+, Cu2+, and Zn2+ was investigated. The raw jute fabric was treated with sodium hydroxide or sodium chlorite to selectively remove hemicelluloses and lignin, respectively. All jute fabrics were characterized by determination of their chemical composition as well as functional group content. The effects of solution pH, contact time, and initial metal ion concentration on the biosorption from monometallic and polymetallic solution by jute fabrics were investigated. The maximum biosorption capacity for all heavy metal ions was observed at pH 5.5. Concerning the contact time, the raw jute fabric shows more than 72 % of the total uptake capacity of Ni2+, Cu2+, and Zn2+ within 1 h, while the jute fabrics with lower hemicelluloses and lignin content show between 72–85 % of the total uptake capacity within 3 h. Increased initial metal ion concentration from 10 to 20 mg/l in monometallic solution caused an increase in the total uptake capacity of jute fabrics with lower hemicelluloses and lignin content for 47–69 % (Ni2+), 42–63 % (Cu2+), and 22–37 % (Zn2+). The biosorption capacity of alkali treated jute fabrics was affected by the changes in the total amount of carboxyl and aldehyde groups that accompany the hemicelluloses removal. In the case of the oxidative treatment, the biosorption capacity was affected by the lignin content as well as the amount of introduced carboxyl groups. The best biosorption performance possesses jute fabric with 63.2 % lower lignin content as well as 81.1 % higher amount of carboxyl groups; biosorption capacity toward Ni2+, Cu2+, and Zn2+ in monometallic solution is about 2.4; 2.2 and 3.5 times higher compared to the raw jute fabric, respectively. All jute fabrics exhibited the same affinity order (which is independent on the initial metal ion concentrations) toward heavy metal ions: Ni2+ > Cu2+ > Zn2+ in the case of competitive biosorption. An increase in the initial metal ion concentration for two times in the polymetallic solution caused about a 35–59 % increase in the total uptake capacity of Ni2+, while the total uptake capacities of Cu2+ and Zn2+ increased for 19–38 % and 18–65 %, respectively.en
dc.publisherSpringeren
dc.relationinfo:eu-repo/grantAgreement/MESTD/Basic Research (BR or ON)/172029/RS//
dc.rightsrestrictedAccess
dc.sourceFibers and Polymersen
dc.subjectWaste jute
dc.subjectHemicelluloses
dc.subjectLignin
dc.subjectBiosorption
dc.subjectHeavy metal ions
dc.titleWaste Jute Fabric as a Biosorbent for Heavy Metal Ions from Aqueous Solutionen
dc.typearticleen
dc.rights.licenseARR
dcterms.abstractAсановић, Ковиљка; Дојчиновић, Биљана; Павун, Л.; Малетић, С.; Ивановска, A.; Костиц, М.;
dc.rights.holderSpringer
dc.citation.volume21
dc.citation.issue9
dc.citation.spage1992
dc.citation.epage2002
dc.citation.rankM21~
dc.identifier.doi10.1007/s12221-020-9639-8
dc.identifier.scopus2-s2.0-85093968918
dc.identifier.wos000581023100013
dc.type.versionpublishedVersion


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record