Investigation of ZnFe2O4 spinel ferrite nanocrystalline screen‐printed thick films for application in humidity sensing
Authorized Users Only
AuthorsNikolić, Maria Vesna
Pavlović, Vera P.
Pavlović, Vladimir B.
Article (Published version)
MetadataShow full item record
Zinc ferrite nanocrystalline powder was obtained by solid state synthesis of starting zinc oxide and hematite nanopowders. Field emission scanning electron microscopy (FESEM and transmission electron microscopy (TEM), X‐ray diffraction (XRD), X‐ray photoelectron spectroscopy (XPS) and Raman spectroscopy confirmed the formation of nanocrystalline zinc‐ferrite powder with a mixed spinel structure with small amounts of remaining zinc oxide and hematite as impurities. Thick film paste was formed and screen printed on test interdigitated PdAg electrodes on alumina substrate. Formation of a porous nanocrystalline structure was confirmed by scanning electron microscopy (SEM) and Hg porosimetry. Humidity sensing properties of zinc ferrite thick films were investigated by monitoring the change in impedance in the relative humidity interval 30‐90% in the frequency range 42 Hz – 1 MHz at room temperature (25 °C) and 50 °C. At 42 Hz at both analyzed temperatures the impedance reduced ~ 46 times in... the humidity range 30‐90%. The dominant influence of grain boundaries was confirmed by analysis of complex impedance with an equivalent circuit.
Keywords:zinc ferrite / nanocrystalline powders / screen‐printed thick films / solid state synthesis / field emission scanning electron microscopy (FESEM) / transmission electron microscopy (TEM) / X‐ray diffraction (XRD) / X‐ray photoelectron spectroscopy (XPS) / Raman spectroscopy
Source:International Journal of Applied Ceramic Technology, 2019, 16, 3, 981-993
- John Wiley & Sons, Inc.
- Zero- to Three-Dimensional Nanostructures for Application in Electronics and Renewable Energy Sources: Synthesis, Characterization and Processing (RS-45007)
- Lithium-ion batteries and fuel cells - research and development (RS-45014)