The effect of current density, deoisition time and electrolytic pH value on roughness of copper coatings
Uticaj gustine struje, vremena taloženja i pH – vrednosti elektrolita na hrapavost prevlaka bakra
Апстракт
The copper coatings were electrodeposited directly onto aluminium from the bath: (CuSO4 (55 g/dm3) + CH2 NH2 - CH2OH (100g/ dm3) + (NH4)2SO4 (30 g/dm3) + Na2SO4(10H2O (75g/dm3) + Na2CO3 (3g/dm3), room temperature, j = 0.3 - 0.8 A/dm2, pH = 10.3-8.5. The copper coatings deposited onto Al show good adhesion. Removal of passive oxide film from aluminium surface was chemically accomplished in solutions 1-4. The effect of current density, deposition time and electrolytic pH on roughness of copper coatings were studied. Roughness of Cu coatings was measured by TR200.
Prevlake bakra taložene su neposredno galvanostatskim putem na aluminijum iz kupatila sastava: [CuSO4 (55 g/dm3) + CH2 NH2 - CH2OH (100 g/dm3) + (NH4)2SO4 (30 g/ dm3) + Na2SO4(10H2O (75 g/dm3) + Na2CO3 (3 g/dm3], temperatura sobna j =0,3-0,8A/dm2, pH = 10,3-8.5. Istaložene prevlake bakra na aluminijumu imaju dobru adheziju. Uklanjanje pasivne oksidne opne sa površine aluminijuma vršeno je hemijski u rastvorima 1-4. Ispitivan je uticaj gustine struje vremena taloženja i pH-vrednosti elektrolita na hrapavost prevlaka bakra. Merenje hrapavosti prevlaka bakra vršeno je pomoću uređaja TR200.
Кључне речи:
electrochemical deposition of coatings / chemical preparation / current density / deposition time / pH-value / roughness / elektrohemijsko taloženje metala / hemijska priprema / gustine struje / vreme taloženja / pH-vrednost / hrapavostИзвор:
Zaštita materijala, 2006, 47, 2, 11-16Издавач:
- Belgrade, Serbia : Engineering Society for Corrosion
Институција/група
IHTMTY - JOUR AU - Tomić, Milorad V. AU - Pavlović, Ljubica AU - Pavlović, Miomir PY - 2006 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/269 AB - The copper coatings were electrodeposited directly onto aluminium from the bath: (CuSO4 (55 g/dm3) + CH2 NH2 - CH2OH (100g/ dm3) + (NH4)2SO4 (30 g/dm3) + Na2SO4(10H2O (75g/dm3) + Na2CO3 (3g/dm3), room temperature, j = 0.3 - 0.8 A/dm2, pH = 10.3-8.5. The copper coatings deposited onto Al show good adhesion. Removal of passive oxide film from aluminium surface was chemically accomplished in solutions 1-4. The effect of current density, deposition time and electrolytic pH on roughness of copper coatings were studied. Roughness of Cu coatings was measured by TR200. AB - Prevlake bakra taložene su neposredno galvanostatskim putem na aluminijum iz kupatila sastava: [CuSO4 (55 g/dm3) + CH2 NH2 - CH2OH (100 g/dm3) + (NH4)2SO4 (30 g/ dm3) + Na2SO4(10H2O (75 g/dm3) + Na2CO3 (3 g/dm3], temperatura sobna j =0,3-0,8A/dm2, pH = 10,3-8.5. Istaložene prevlake bakra na aluminijumu imaju dobru adheziju. Uklanjanje pasivne oksidne opne sa površine aluminijuma vršeno je hemijski u rastvorima 1-4. Ispitivan je uticaj gustine struje vremena taloženja i pH-vrednosti elektrolita na hrapavost prevlaka bakra. Merenje hrapavosti prevlaka bakra vršeno je pomoću uređaja TR200. PB - Belgrade, Serbia : Engineering Society for Corrosion T2 - Zaštita materijala T1 - The effect of current density, deoisition time and electrolytic pH value on roughness of copper coatings T1 - Uticaj gustine struje, vremena taloženja i pH – vrednosti elektrolita na hrapavost prevlaka bakra VL - 47 IS - 2 SP - 11 EP - 16 UR - https://hdl.handle.net/21.15107/rcub_cer_269 ER -
@article{ author = "Tomić, Milorad V. and Pavlović, Ljubica and Pavlović, Miomir", year = "2006", abstract = "The copper coatings were electrodeposited directly onto aluminium from the bath: (CuSO4 (55 g/dm3) + CH2 NH2 - CH2OH (100g/ dm3) + (NH4)2SO4 (30 g/dm3) + Na2SO4(10H2O (75g/dm3) + Na2CO3 (3g/dm3), room temperature, j = 0.3 - 0.8 A/dm2, pH = 10.3-8.5. The copper coatings deposited onto Al show good adhesion. Removal of passive oxide film from aluminium surface was chemically accomplished in solutions 1-4. The effect of current density, deposition time and electrolytic pH on roughness of copper coatings were studied. Roughness of Cu coatings was measured by TR200., Prevlake bakra taložene su neposredno galvanostatskim putem na aluminijum iz kupatila sastava: [CuSO4 (55 g/dm3) + CH2 NH2 - CH2OH (100 g/dm3) + (NH4)2SO4 (30 g/ dm3) + Na2SO4(10H2O (75 g/dm3) + Na2CO3 (3 g/dm3], temperatura sobna j =0,3-0,8A/dm2, pH = 10,3-8.5. Istaložene prevlake bakra na aluminijumu imaju dobru adheziju. Uklanjanje pasivne oksidne opne sa površine aluminijuma vršeno je hemijski u rastvorima 1-4. Ispitivan je uticaj gustine struje vremena taloženja i pH-vrednosti elektrolita na hrapavost prevlaka bakra. Merenje hrapavosti prevlaka bakra vršeno je pomoću uređaja TR200.", publisher = "Belgrade, Serbia : Engineering Society for Corrosion", journal = "Zaštita materijala", title = "The effect of current density, deoisition time and electrolytic pH value on roughness of copper coatings, Uticaj gustine struje, vremena taloženja i pH – vrednosti elektrolita na hrapavost prevlaka bakra", volume = "47", number = "2", pages = "11-16", url = "https://hdl.handle.net/21.15107/rcub_cer_269" }
Tomić, M. V., Pavlović, L.,& Pavlović, M.. (2006). The effect of current density, deoisition time and electrolytic pH value on roughness of copper coatings. in Zaštita materijala Belgrade, Serbia : Engineering Society for Corrosion., 47(2), 11-16. https://hdl.handle.net/21.15107/rcub_cer_269
Tomić MV, Pavlović L, Pavlović M. The effect of current density, deoisition time and electrolytic pH value on roughness of copper coatings. in Zaštita materijala. 2006;47(2):11-16. https://hdl.handle.net/21.15107/rcub_cer_269 .
Tomić, Milorad V., Pavlović, Ljubica, Pavlović, Miomir, "The effect of current density, deoisition time and electrolytic pH value on roughness of copper coatings" in Zaštita materijala, 47, no. 2 (2006):11-16, https://hdl.handle.net/21.15107/rcub_cer_269 .