dc.description.abstractThis paper considers the influence of nitrogen in the shielding gas during TIG welding as well as the influence of a welding current level on the resistance to pitting corrosion and intergranular corrosion in welded joints of X5CrNi18-10 stainless steel. Testing of pitting corrosion was carried out using the potentiodynamic method, while intergranular corrosion was tested with the Double-Loop Electrochemical Potentiokinetic Reactivation method. Pitting corrosion resistance of welded joints (the weld metal and the heat affected zone) is higher in the presence of nitrogen in the shielding gas, while integranular corrosion resistance remains unchanged. Pitting corrosion resistance of the heat affected zone in the welded joint formed in nitrogen-free shielding gas is lower than in the base metal, while the weld metal has similar pitting corrosion resistance as the base metal. With an increase in a welding current level, pitting corrosion resistance and resistance to intergranular corrosion of welded joints decrease. The passivation current density is shown to be a good indicator of pitting corrosion resistance of welded joints. Hardness values of the weld metal and the heat affected zone are slightly lower than the base metal hardness value.en
dc.publisherElsevier
dc.relationinfo:eu-repo/grantAgreement/MESTD/Technological Development (TD or TR)/34028/RS//
dc.relationinfo:eu-repo/grantAgreement/MESTD/Technological Development (TD or TR)/35021/RS//
dc.rightsrestrictedAccess
dc.sourceJournal of Materials Processing Technology
dc.subjectIntergranular corrosionen
dc.subjectNitrogenen
dc.subjectPitting corrosionen
dc.subjectStainless steelen
dc.subjectWeldingen
dc.titleCorrosion resistance of welded joints of X5CrNi18-10 stainless steelen
dc.typearticle
dc.rights.licenseARR
dcterms.abstractРадовановић, Лидија Д.; Бобић, Биљана; Јегдић, Боре; Радојковић, Бојана; Aлић, Бехар;
dc.citation.volume266
dc.citation.spage579
dc.citation.epage587
dc.citation.other266: 579-587
dc.citation.rankaM21
dc.identifier.doi10.1016/j.jmatprotec.2018.11.029
dc.identifier.scopus2-s2.0-85057347749
dc.identifier.wos000456757200053
dc.type.versionpublishedVersion


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record