dc.description.abstractCrystalline calcium titanate was synthesized by mechanical activation of a mixture of CaO, obtained by thermal treatment of CaCO3, and TiO 2 in anatase or rutile form, in a planetary ball mill for 30, 60, 120 and 240 min.. The effect of milling on the solid-state reaction was followed by X-ray diffraction. Changes in powder size and morphology due to milling were determinate by SEM, while BET analysis was made to determine the specific surface area of powders. It was pointed out that the formation of calcium titanate was more easily achieved by mechanical activation synthesis of the mixture of calcium oxide and anatase modification of titanium oxide compared to the rutile form.en
dc.rightsopenAccess
dc.sourceMaterials Science Forum
dc.subjectCaTiO3en
dc.subjectMechanochemical synthesisen
dc.subjectPlanetary ball millen
dc.titleMechanically activated synthesis of CaTiO3 from mixture of CaO and TiO2en
dc.typeconferenceObject
dc.rights.licenseARR
dcterms.abstractВукотиц, В.М.; Стојановиц, Б.; Вуковић, Зорица; Радојевиц, Н.; Зивковиц, Љ.;
dc.citation.volume494
dc.citation.spage393
dc.citation.epage398
dc.citation.other494: 393-398
dc.citation.rankM23
dc.identifier.doi10.4028/www.scientific.net/MSF.494.393
dc.identifier.scopus2-s2.0-35248829052
dc.identifier.wos000230985800065
dc.type.versionpublishedVersion


Документи

Thumbnail

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу