Uticaj jačine struje zavarivanja na sklonost prema interkristalnoj koroziji zavarenog spoja nerdajućeg čelika

dc.creatorJegdić, Bore
dc.creatorBobić, Biljana
dc.creatorAlić, Behar
dc.date.accessioned2019-01-30T17:53:03Z
dc.date.available2019-01-30T17:53:03Z
dc.date.issued2017
dc.identifier.issn0354-7965
dc.identifier.urihttp://cer.ihtm.bg.ac.rs/handle/123456789/2081
dc.description.abstractSusceptibility to intergranular corrosion in welded joints of austenitic stainless steel X5Cr-Ni18-10 was tested. The welding was performed with different intensity of welding current (110 A, 130 A and 150 A). The tests were performed using electrochemical potentiokinetic reactivation method with double loop (DL EPR method) on the base metal and in the heat affected zone. The results obtained by the DL EPR method show that the heat affected zone formed by welding with 150 A has the highest susceptibility to intergranular corrosion. The susceptibility to intergranular corrosion is considerably lower when applying smaller welding current. The base metal is resistant to intergranular corrosion. The indicator of susceptibility to intergranular corrosion (Qr/Qp)GBA is ~ 6 times higher for the heat affected zone (at 150 A welding current intensity) than for the base metal. Obtained testing results show that the welding current intensity greatly influences the susceptibility to intergranular corrosion in welded joints of stainless steel X5Cr-Ni18-10.en
dc.description.abstractIspitana je sklonost prema interkristalnoj koroziji zavarenog spoja austenitnog nerđajućeg čelika X5Cr-Ni18-10. Zavareni spoj je formiran pri različitim jačinama struje zavarivanja (110 A, 130 A i 150 A). Ispitivanja su vršena metodom elektrohemijske potenciokinetičke reaktivacije sa dvostrukom petljom (DL EPR metoda), na osnovnom metalu i u zoni uticaja toplote (ZUT). Osnovni metal je otporan prema interkristalnoj koroziji. Zona uticaja toplote formirana pri zavarivanju strujom jačine 150 A pokazuje najveću sklonost prema interkristalnoj koroziji. Sklonost prema interkristalnoj koroziji je znatno niža pri zavarivanju manjim jačinama struje. Pokazatelj sklonosti prema interkristalnoj koroziji (Qr/Qp)GBA je ~ 6 puta veći za zonu uticaja toplote (pri jačini struje zavarivanja od 150 A) nego za osnovni metal. Na osnovu prikazanih rezultata može se zaključiti da jačina struje zavarivanja u velikoj meri utiče na sklonost zavarenog spoja nerđajućeg čelika X5CrNi18-10 prema interkristalnoj koroziji. .sr
dc.publisherDUZS - Društvo za unapređivanje zavarivanja u Srbiji, Beograd
dc.relationinfo:eu-repo/grantAgreement/MESTD/Technological Development (TD or TR)/34028/RS//
dc.relationinfo:eu-repo/grantAgreement/MESTD/Technological Development (TD or TR)/34016/RS//
dc.rightsopenAccess
dc.sourceZavarivanje i zavarene konstrukcije
dc.subjectstainless steelsen
dc.subjectwelded jointsen
dc.subjectintergranular corrosionen
dc.subjecttest methodsen
dc.subjectnerđajući čelicisr
dc.subjectzavareni spojsr
dc.subjectinterkristalna korozijasr
dc.subjectmetode ispitivanjasr
dc.titleInfluence of welding current intensity on susceptibility to intergranular corrosion in welded joints of stainless steelen
dc.titleUticaj jačine struje zavarivanja na sklonost prema interkristalnoj koroziji zavarenog spoja nerdajućeg čelikasr
dc.typearticle
dc.rights.licenseARR
dcterms.abstractБобић, Биљана; Aлић, Бехар; Јегдић, Боре; Утицај јачине струје заваривања на склоност према интеркристалној корозији завареног споја нердајућег челика; Утицај јачине струје заваривања на склоност према интеркристалној корозији завареног споја нердајућег челика;
dc.citation.volume62
dc.citation.issue4
dc.citation.spage149
dc.citation.epage154
dc.citation.other62(4): 149-154
dc.citation.rankM51
dc.identifier.doi10.5937/zzk1704149J
dc.identifier.rcubConv_385
dc.identifier.fulltexthttp://cer.ihtm.bg.ac.rs//bitstream/id/8512/2079.pdf
dc.type.versionpublishedVersion


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record