Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic
(Belgrade : International Institute for the Science of Sintering, 2017)
Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation ...
Damage level evaluation of zircon samples caused by cavitation erosion using image analysis
(Bor : University of Belgrade - Technical Faculty in Bor, 2017)
This study is focused on monitoring the degradation level of zircon based ceramic materials during exposure to cavitation. In addition to conventional degradation monitoring methods, weight loss measuring, the emphasis is ...
Investigation of image analysis on comparison of cavitation erosion degradation of mullite and zircon samples based
(Institute for Multidisciplinary Research, University of Belgrade, 2017)
Mulilte and zircon are widely used for different applications for refractory materials. In this paper their behavior in conditions of the cavitation erosion was investigated. Cavitation erosion testing was applied using ...
Comparison of cavitation erosion resistance of mullite and zircon samples based on non destructive characterization
(Association of Metallurgical Engineers of Serbia (AMES), 2017)
Mullite and zircon are widely used for different applications for refractory materials. In this paper their cavitation erosion resistance will be investigated. Cavitation erosion resistance testing will be applied using ...
Implementation of infrared thermography on defects monitoring during cavitation erosion of mullite ceramic
(ПП Полiтexперiодика, 2017)
Cavitation erosion of mullite samples was monitored using vibratory cavitation set up with stationary sample. The level of degradation of the sample was monitored using weight loss and image analysis. Thermal imaging ...