Microstructure of LaNiO3 thin films obtained by the spin-on technique from citrate precursors
(Elsevier Sci Ltd, Oxford, 2008)
The morphology of perovskite LaNiO3 (LNO) thin films is a very important feature considering the fact that they could be used as an electrode material in ferroelectric devices. In this work, LNO films were prepared from ...
Biomimetic synthesis and properties of cellular SiC
(Elsevier Sci Ltd, Oxford, 2014)
Biomorphous beta-SiC ceramics were produced from several species of wood such as ash, wild cherry, black alder, Persian walnut, sessile oak and European hornbeam. The wood was pyrolysed, impregnated with tetraethyl ...
The synthesis of single phase WC nanoparticles/C composite by solid state reaction involving nitrogen-rich carbonized polyaniline
(Elsevier Sci Ltd, Oxford, 2013)
Single phase tungsten carbide nanoparticles (WC-NPs), (mean particle diameter 5.4 nm), distributed over carbonized polyaniline (C-PANT) nanotubes/nanosheets were synthesized by a solid state reaction between WO3 and ...
Porous ceramic monoliths based on diatomite
(Elsevier Sci Ltd, Oxford, 2015)
Porous silica ceramics were obtained at low forming pressure and low sintering temperature by using diatomaceous earth as a silica source and boric acid as an inexpensive additive. The starting raw material, diatomite from ...
Structural investigation of mechanically activated nanocrystalline BaTiO3 powders
(Elsevier Sci Ltd, Oxford, 2011)
In this article, in order to obtain tetragonal nanocrystalline BaTiO3, structural investigations of mechanically activated BaTiO3 powder have been performed. A mercury porosimetry analysis and scanning electron microscopy ...
Morphology investigation of mechanically activated ZnO-SnO2 system
(Elsevier Sci Ltd, Oxford, 2008)
Powder mixtures of zinc oxide and tin oxide in the molar ratio, ZnO:SnO2 = 2:1, were mechanically activated in a planetary ball mill in the time intervals of 0-160 min. The adsorption-desorption isotherms, specific surface ...
Preparation and characterization of clay-based porous ceramics with boric acid as additive
(Elsevier Sci Ltd, Oxford, 2014)
Intention of this work was to obtain porous silicon dioxide ceramics by using boric acid as an inexpensive additive at low forming pressure and low sintering temperature. Starting raw material, smectite clay from surface ...