Show simple item record

dc.creatorKokunesoski, Maja
dc.creatorŠaponjić, Aleksandra
dc.creatorStanković, Miroslav
dc.creatorMajstorovic, Jelena
dc.creatorEgelja, Adela
dc.creatorIlić, Svetlana
dc.creatorMatović, Branko
dc.date.accessioned2019-01-30T17:50:32Z
dc.date.available2019-01-30T17:50:32Z
dc.date.issued2016
dc.identifier.issn0272-8842
dc.identifier.urihttp://cer.ihtm.bg.ac.rs/handle/123456789/1961
dc.description.abstractPorous silica ceramics were obtained at low forming pressure (40-80 MPa) and low sintering temperature (850-1300 degrees C) for 4 h in air. Boric acid was used as a low-cost additive, in the amount of 2 wt%. Relatively high porosities of nearly 40% and 65% are obtained for the samples of clay and diatomite pressed at 40 MPa, and sintered at 1000 degrees C, respectively. The samples sintered at 1150 degrees C and 1300 degrees C have the average pore size diameters in the range of macroporous for clay 0.2-10 m and for diatomite 0.2-5 m. X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy, and mercury porosimetry measurements were employed to characterize of the obtained samples. Measurements of densities and open porosities by immersion technique were used, according to the Archimedes principle. The relations between mechanical characteristics of the samples formed by using different pressures and sintered at different temperature, were discussed.en
dc.publisherElsevier Sci Ltd, Oxford
dc.relationinfo:eu-repo/grantAgreement/MESTD/Integrated and Interdisciplinary Research (IIR or III)/45012/RS//
dc.rightsrestrictedAccess
dc.sourceCeramics International
dc.subjectSinteringen
dc.subjectPorosityen
dc.subjectClaysen
dc.subjectDiatomiteen
dc.subjectBoric aciden
dc.titleEffect of boric acid on the porosity of clay and diatomite monolithsen
dc.typearticle
dc.rights.licenseARR
dcterms.abstractЕгеља, Aдела; Илиц, Светлана; Сапоњиц, Aлександра; Кокунесоски, Маја; Матовић, Бранко; Мајсторовиц, Јелена; Станковић, Мирослав;
dc.citation.volume42
dc.citation.issue5
dc.citation.spage6383
dc.citation.epage6390
dc.citation.other42(5): 6383-6390
dc.citation.rankaM21
dc.identifier.doi10.1016/j.ceramint.2016.01.034
dc.identifier.rcubConv_3496
dc.identifier.scopus2-s2.0-84955316901
dc.identifier.wos000370884500094
dc.type.versionpublishedVersion


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record