The effect of preparation of aluminum surface on surface reflection

Abstract

Aluminum samples were electrochemically polished in one of three solutions for electrochemical polishing. On those samples the surface reflection was measured. The effect of the anode treatment as the interface between the chemical preparation and electrochemical polishing on the surface reflection was shown. Based on the results it can be concluded that among all the solutions investigated, the most efficient solution for electrochemical polishing is the solution number II. Aluminum samples treated with this solution have the greatest reflection. The effects of temperature change and stirring on the aluminum reflection were also investigated. It was shown that mirror brightness of metal surfaces can be associated with the high degree of mirror reflection which approaches very nearly the ideal reflectance of the same metal, with the small degree of diffuse reflection.

Uzorci aluminijuma su podvrgavani elektrohemijskom glačanju u jednom od tri rastvora za elektrohemijsko glačanje. Na tako pripremljenim uzorcima merena je površinska refleksija svetlosti. Pokazan je i uticaj anadne obrade kao među faze između hemijske pripreme i elektrohemijskog glačanja na refleksiju aluminijuma. Na osnovu dobijenih rezultata može se zaključiti da je od ispitivanih rastvora za elektrohemijsko glačanje, najefikasniji rastvor II. Uzorci aluminijuma tretirani u ovom rastvoru imaju najveću refleksiju. Takođe je ispitivan i uticaj promene temperature i mešanja rastvora na refleksiju aluminijuma. Pokazano je da se ogledalski sjaj metalnih površina može povezati sa visokim stepenom ogledalske refleksije svetlosti, koji se približava idealnoj refleksivnosti istog metala, uz što manji stepen difuzne refleksije.