Show simple item record

dc.creatorPočuča-Nešić, Milica
dc.creatorBranković, Goran
dc.creatorBernik, Slavko
dc.creatorRečnik, Aleksander
dc.creatorVasiljević-Radović, Dana
dc.creatorBranković, Zorica
dc.date.accessioned2019-01-30T17:30:31Z
dc.date.available2019-01-30T17:30:31Z
dc.date.issued2012
dc.identifier.issn1820-6131
dc.identifier.urihttps://cer.ihtm.bg.ac.rs/handle/123456789/1009
dc.description.abstractLanthanum nickelate (LNO) is a perovskite oxide material with metallic conductivity in a wide temperature range which makes it suitable for application as electrode material for thin films. In this paper LNO thin films were prepared by polymerizable complex method from the diluted citrate solutions. Precursor solutions were spin coated onto Si-substrates with amorphous layer of SiO2. Deposited layers were thermally treated from the substrate side with low heating rate (1°/min) up to 700°C and finally annealed for 10 hours. Results of AFM and FESEM showed that films are very smooth (Ra = 4 nm), dense, crack-free and with large square-shaped grains (170 nm). According to FESEM and TEM results the obtained four-layered film was only 65 nm thin. EBSD and XRD analyses confirmed polycrystalline microstructure of the films without preferential orientation. It was concluded that the presence of SiO2 layer on Si substrate prevents epitaxial or oriented growth of LNO.en
dc.publisherUniversity of Novi Sad
dc.relationProject MESTD
dc.rightsopenAccess
dc.rights.urihttps://creativecommons.org/licenses/by-nc-nd/4.0/
dc.sourceProcessing and Application of Ceramics
dc.subjectlanthanum nickelateen
dc.subjectfilmsen
dc.subjectelectron microscopyen
dc.subjectmicrostructureen
dc.titleTEM and FESEM investigation of lanthanum nickelate thin films obtained by chemical solution depositionen
dc.typearticle
dc.rights.licenseBY-NC-ND
dcterms.abstractВасиљевић-Радовић, Дана; Бранковић, Зорица; Бранковић, Горан; Берник, Славко; Почуча-Нешић, Милица; Речник, Aлександер;
dc.citation.volume6
dc.citation.issue2
dc.citation.spage103
dc.citation.epage107
dc.citation.other6(2): 103-107
dc.citation.rankM51
dc.identifier.doi10.2298/PAC1202103P
dc.identifier.fulltexthttps://cer.ihtm.bg.ac.rs//bitstream/id/7574/1007.pdf
dc.type.versionpublishedVersion


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record