Cavitation damage of mullite ceramic: implementation of image analysis
(Bor : University of Belgrade - Technical Faculty in BorBor : Mining and Metallurgy Institute Bor, 2016)
The paper presents the results of testing the mullite ceramics in terms of cavitation erosion. Mullite samples were sintered at 1200 °C. To determine the cavitation resistance the ultrasonic vibration method with stationary ...
Damage level evaluation of zircon samples caused by cavitation erosion using image analysis
(Bor : University of Belgrade - Technical Faculty in Bor, 2017)
This study is focused on monitoring the degradation level of zircon based ceramic materials during exposure to cavitation. In addition to conventional degradation monitoring methods, weight loss measuring, the emphasis is ...
Anisotropy of refractory concrete subjected to the thermal shock by using the surface analysis
(Bor : University of Belgrade - Technical Faculty in Bor, 2013)
Monitoring and analysis of the material anisotropy during the thermal shock of the refractory concrete was studied. The material was alumina based low cement castable pre-treated at 1300°C for 3 hours. Water quench test ...