TY  - CONF
AU  - Majstorović, Jelena
AU  - Martinović, Sanja
AU  - Vlahović, Milica
AU  - Dojčinović, Marina
AU  - Pavlović, Marko
AU  - Volkov Husović, Tatjana
PY  - 2018
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/6012
AB  - Samples based on talc with 15 % of zeolite from Zlatokop, Serbia, sintered at 1200 ºC were prepared and tested in condition of cavitation erosion. The ultrasonic vibratory cavitation set up with a stationary specimen was used. Mass loss was measured and degradation level of the samples using image analysis and Young modulus of elasticity was monitored. Obtained results showed good resistance to the cavitation erosion giving the possibility of future application in different conditions where cavitation erosion is expected.
PB  - Bosnia and Herzegovina : University of Zenica,  Faculty of metallurgy and technology
C3  - Proceedings - 12th Scientific/Research Symposium With International Participation “Metallic and Nonmetallic Materials: Production-properties-application“, , April 19th – 20th 2018., Vlašić, Bosnia and Herzegovina
T1  - Cavitation of refractory samples based on talc and zeolite from Zlatokop
SP  - 230
EP  - 233
UR  - https://hdl.handle.net/21.15107/rcub_cer_6012
ER  - 

@conference{
author = "Majstorović, Jelena and Martinović, Sanja and Vlahović, Milica and Dojčinović, Marina and Pavlović, Marko and Volkov Husović, Tatjana",
year = "2018",
abstract = "Samples based on talc with 15 % of zeolite from Zlatokop, Serbia, sintered at 1200 ºC were prepared and tested in condition of cavitation erosion. The ultrasonic vibratory cavitation set up with a stationary specimen was used. Mass loss was measured and degradation level of the samples using image analysis and Young modulus of elasticity was monitored. Obtained results showed good resistance to the cavitation erosion giving the possibility of future application in different conditions where cavitation erosion is expected.",
publisher = "Bosnia and Herzegovina : University of Zenica,  Faculty of metallurgy and technology",
journal = "Proceedings - 12th Scientific/Research Symposium With International Participation “Metallic and Nonmetallic Materials: Production-properties-application“, , April 19th – 20th 2018., Vlašić, Bosnia and Herzegovina",
title = "Cavitation of refractory samples based on talc and zeolite from Zlatokop",
pages = "230-233",
url = "https://hdl.handle.net/21.15107/rcub_cer_6012"
}

Majstorović, J., Martinović, S., Vlahović, M., Dojčinović, M., Pavlović, M.,& Volkov Husović, T.. (2018). Cavitation of refractory samples based on talc and zeolite from Zlatokop. in Proceedings - 12th Scientific/Research Symposium With International Participation “Metallic and Nonmetallic Materials: Production-properties-application“, , April 19th – 20th 2018., Vlašić, Bosnia and Herzegovina
Bosnia and Herzegovina : University of Zenica,  Faculty of metallurgy and technology., 230-233.
https://hdl.handle.net/21.15107/rcub_cer_6012

Majstorović J, Martinović S, Vlahović M, Dojčinović M, Pavlović M, Volkov Husović T. Cavitation of refractory samples based on talc and zeolite from Zlatokop. in Proceedings - 12th Scientific/Research Symposium With International Participation “Metallic and Nonmetallic Materials: Production-properties-application“, , April 19th – 20th 2018., Vlašić, Bosnia and Herzegovina. 2018;:230-233.
https://hdl.handle.net/21.15107/rcub_cer_6012 .

Majstorović, Jelena, Martinović, Sanja, Vlahović, Milica, Dojčinović, Marina, Pavlović, Marko, Volkov Husović, Tatjana, "Cavitation of refractory samples based on talc and zeolite from Zlatokop" in Proceedings - 12th Scientific/Research Symposium With International Participation “Metallic and Nonmetallic Materials: Production-properties-application“, , April 19th – 20th 2018., Vlašić, Bosnia and Herzegovina (2018):230-233,
https://hdl.handle.net/21.15107/rcub_cer_6012 .

TY  - JOUR
AU  - Majstorović-Necković, Jelena B.
AU  - Pavlović, Marko D.
AU  - Dojčinović, Marina
AU  - Martinović, Sanja
AU  - Vlahović, Milica
AU  - Volkov-Husović, Tatjana
PY  - 2018
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/2281
AB  - Using domestic zeolite from Igroš as row material for ceramic samples for application in condition of cavitation erosion. Samples based on talc with 15 % of zeolite, from Igroš, sintered at 1200oC were used in this investigation. The ultrasonic vibratory cavitation set up with stacionary specimen was used. Mass loss was measured and degradation level of the samples using image analysis and Young modulus of elasticity. Obtained results showed good resistance of the sample to the cavitation erosion, which give the possibility for possible future application of ceramic samples based on talc and yeolite in different conditions where cavitation erosion is expected.
AB  - U radu su prezentirani rezultati istraživanja korišćenja domaćeg zeolita sa ležišta 'Igroš' za izradu keramičkih uzoraka i primenu u uslovima dejstva kavitacije. Za ispitivanja su korišćeni uzorci talka sa 15% zeolita iz domaćeg ležišta IGROŠ (Brus) sinterovani na 1200oC. Za određivanje otpornosti na dejstvo kavitacije korišćena je ultrazvučna vibraciona metoda sa stacionarnim uzorkom. Gubitak mase i nivo degradacije površine uzoraka praćeni su primenom analize slike i Jungovog modula elastičnosti. Rezultati ispitivanja pokazali su dobru otpornost keramike na dejstvo kavitacije na bazi talka i zeolita što ukazuje na mogućnost primene u različitim oblastima industrije gde se očekuje prisustvo razaranja pod dejstvom kavitacije.
PB  - Srbija : Savez inženjera i tehničara Srbije
T2  - Tehnika
T1  - Cavitation of refratory samples based on talc and domestic zeolite
T1  - Ispitivanje vatrostalnih uzoraka na bazi talka i domaćeg zeolita na dejstvo kavitacije
VL  - 73
IS  - 3
SP  - 364
EP  - 369
DO  - 10.5937/tehnika1803364M
ER  - 

@article{
author = "Majstorović-Necković, Jelena B. and Pavlović, Marko D. and Dojčinović, Marina and Martinović, Sanja and Vlahović, Milica and Volkov-Husović, Tatjana",
year = "2018",
abstract = "Using domestic zeolite from Igroš as row material for ceramic samples for application in condition of cavitation erosion. Samples based on talc with 15 % of zeolite, from Igroš, sintered at 1200oC were used in this investigation. The ultrasonic vibratory cavitation set up with stacionary specimen was used. Mass loss was measured and degradation level of the samples using image analysis and Young modulus of elasticity. Obtained results showed good resistance of the sample to the cavitation erosion, which give the possibility for possible future application of ceramic samples based on talc and yeolite in different conditions where cavitation erosion is expected., U radu su prezentirani rezultati istraživanja korišćenja domaćeg zeolita sa ležišta 'Igroš' za izradu keramičkih uzoraka i primenu u uslovima dejstva kavitacije. Za ispitivanja su korišćeni uzorci talka sa 15% zeolita iz domaćeg ležišta IGROŠ (Brus) sinterovani na 1200oC. Za određivanje otpornosti na dejstvo kavitacije korišćena je ultrazvučna vibraciona metoda sa stacionarnim uzorkom. Gubitak mase i nivo degradacije površine uzoraka praćeni su primenom analize slike i Jungovog modula elastičnosti. Rezultati ispitivanja pokazali su dobru otpornost keramike na dejstvo kavitacije na bazi talka i zeolita što ukazuje na mogućnost primene u različitim oblastima industrije gde se očekuje prisustvo razaranja pod dejstvom kavitacije.",
publisher = "Srbija : Savez inženjera i tehničara Srbije",
journal = "Tehnika",
title = "Cavitation of refratory samples based on talc and domestic zeolite, Ispitivanje vatrostalnih uzoraka na bazi talka i domaćeg zeolita na dejstvo kavitacije",
volume = "73",
number = "3",
pages = "364-369",
doi = "10.5937/tehnika1803364M"
}

Majstorović-Necković, J. B., Pavlović, M. D., Dojčinović, M., Martinović, S., Vlahović, M.,& Volkov-Husović, T.. (2018). Cavitation of refratory samples based on talc and domestic zeolite. in Tehnika
Srbija : Savez inženjera i tehničara Srbije., 73(3), 364-369.
https://doi.org/10.5937/tehnika1803364M

Majstorović-Necković JB, Pavlović MD, Dojčinović M, Martinović S, Vlahović M, Volkov-Husović T. Cavitation of refratory samples based on talc and domestic zeolite. in Tehnika. 2018;73(3):364-369.
doi:10.5937/tehnika1803364M .

Majstorović-Necković, Jelena B., Pavlović, Marko D., Dojčinović, Marina, Martinović, Sanja, Vlahović, Milica, Volkov-Husović, Tatjana, "Cavitation of refratory samples based on talc and domestic zeolite" in Tehnika, 73, no. 3 (2018):364-369,
https://doi.org/10.5937/tehnika1803364M . .

TY  - JOUR
AU  - Martinović, Sanja
AU  - Vlahović, Milica
AU  - Dojčinović, Marina
AU  - Pavlović, Marko
AU  - Volkov-Husović, Tatjana
PY  - 2018
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/2343
AB  - In this study the resistance of cordierite and zircon to the cavitation erosion was investigated with the aim of possible spreading their application. Cavitation erosion test was applied using standard ultrasonic vibratory set up with stationary sample. Weight loss and image analysis measurements including morphological analysis of the formed pits were used for monitoring degradation during the cavitation erosion testing. The obtained results were discussed in order to compare and analyze degradation mechanism and the resistance of the investigated materials to cavitation erosion. Cordierite sample underwent less serious degradation, characterized by continual forming of new pits, while zircon degradation progressed by growth and merging of already formed pits.
PB  - Elsevier
T2  - Materials Letters
T1  - Comparison of cavitation erosion behavior of cordierite and zircon based samples using image and morphological analyses
VL  - 220
SP  - 136
EP  - 139
DO  - 10.1016/j.matlet.2018.03.029
ER  - 

@article{
author = "Martinović, Sanja and Vlahović, Milica and Dojčinović, Marina and Pavlović, Marko and Volkov-Husović, Tatjana",
year = "2018",
abstract = "In this study the resistance of cordierite and zircon to the cavitation erosion was investigated with the aim of possible spreading their application. Cavitation erosion test was applied using standard ultrasonic vibratory set up with stationary sample. Weight loss and image analysis measurements including morphological analysis of the formed pits were used for monitoring degradation during the cavitation erosion testing. The obtained results were discussed in order to compare and analyze degradation mechanism and the resistance of the investigated materials to cavitation erosion. Cordierite sample underwent less serious degradation, characterized by continual forming of new pits, while zircon degradation progressed by growth and merging of already formed pits.",
publisher = "Elsevier",
journal = "Materials Letters",
title = "Comparison of cavitation erosion behavior of cordierite and zircon based samples using image and morphological analyses",
volume = "220",
pages = "136-139",
doi = "10.1016/j.matlet.2018.03.029"
}

Martinović, S., Vlahović, M., Dojčinović, M., Pavlović, M.,& Volkov-Husović, T.. (2018). Comparison of cavitation erosion behavior of cordierite and zircon based samples using image and morphological analyses. in Materials Letters
Elsevier., 220, 136-139.
https://doi.org/10.1016/j.matlet.2018.03.029

Martinović S, Vlahović M, Dojčinović M, Pavlović M, Volkov-Husović T. Comparison of cavitation erosion behavior of cordierite and zircon based samples using image and morphological analyses. in Materials Letters. 2018;220:136-139.
doi:10.1016/j.matlet.2018.03.029 .

Martinović, Sanja, Vlahović, Milica, Dojčinović, Marina, Pavlović, Marko, Volkov-Husović, Tatjana, "Comparison of cavitation erosion behavior of cordierite and zircon based samples using image and morphological analyses" in Materials Letters, 220 (2018):136-139,
https://doi.org/10.1016/j.matlet.2018.03.029 . .

TY  - CONF
AU  - Pavlović, Marko
AU  - Martinović, Sanja
AU  - Dojčinović, Marina
AU  - Vlahović, Milica
AU  - Stević, Zoran
AU  - Volkov Husović, Tatjana
PY  - 2017
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/7259
AB  - This study is focused on monitoring the degradation level of zircon based ceramic materials during exposure to cavitation. In addition to conventional degradation monitoring methods, weight loss measuring, the emphasis is on monitoring the changes occurring at the surface of the sample by taking the photos and analyzing of these images. In this paper, several parameters are monitored by image analysis: the level of surface degradation, the number of pits, and the average area of the pits. This method proved to be very fast and useful for a quantification of damage which could improve the prediction of the material lifetime.
PB  - Bor : University of Belgrade - Technical Faculty in Bor
C3  - Proceedings - 49th International October Conference on Mining and Metallurgy-IOC-2017, October 18-21 2017, Bor Lake, Serbia
T1  - Damage level evaluation of zircon samples caused by cavitation erosion using image analysis
SP  - 594
EP  - 597
UR  - https://hdl.handle.net/21.15107/rcub_cer_7259
ER  - 

@conference{
author = "Pavlović, Marko and Martinović, Sanja and Dojčinović, Marina and Vlahović, Milica and Stević, Zoran and Volkov Husović, Tatjana",
year = "2017",
abstract = "This study is focused on monitoring the degradation level of zircon based ceramic materials during exposure to cavitation. In addition to conventional degradation monitoring methods, weight loss measuring, the emphasis is on monitoring the changes occurring at the surface of the sample by taking the photos and analyzing of these images. In this paper, several parameters are monitored by image analysis: the level of surface degradation, the number of pits, and the average area of the pits. This method proved to be very fast and useful for a quantification of damage which could improve the prediction of the material lifetime.",
publisher = "Bor : University of Belgrade - Technical Faculty in Bor",
journal = "Proceedings - 49th International October Conference on Mining and Metallurgy-IOC-2017, October 18-21 2017, Bor Lake, Serbia",
title = "Damage level evaluation of zircon samples caused by cavitation erosion using image analysis",
pages = "594-597",
url = "https://hdl.handle.net/21.15107/rcub_cer_7259"
}

Pavlović, M., Martinović, S., Dojčinović, M., Vlahović, M., Stević, Z.,& Volkov Husović, T.. (2017). Damage level evaluation of zircon samples caused by cavitation erosion using image analysis. in Proceedings - 49th International October Conference on Mining and Metallurgy-IOC-2017, October 18-21 2017, Bor Lake, Serbia
Bor : University of Belgrade - Technical Faculty in Bor., 594-597.
https://hdl.handle.net/21.15107/rcub_cer_7259

Pavlović M, Martinović S, Dojčinović M, Vlahović M, Stević Z, Volkov Husović T. Damage level evaluation of zircon samples caused by cavitation erosion using image analysis. in Proceedings - 49th International October Conference on Mining and Metallurgy-IOC-2017, October 18-21 2017, Bor Lake, Serbia. 2017;:594-597.
https://hdl.handle.net/21.15107/rcub_cer_7259 .

Pavlović, Marko, Martinović, Sanja, Dojčinović, Marina, Vlahović, Milica, Stević, Zoran, Volkov Husović, Tatjana, "Damage level evaluation of zircon samples caused by cavitation erosion using image analysis" in Proceedings - 49th International October Conference on Mining and Metallurgy-IOC-2017, October 18-21 2017, Bor Lake, Serbia (2017):594-597,
https://hdl.handle.net/21.15107/rcub_cer_7259 .

TY  - CONF
AU  - Pavlović, Marko
AU  - Martinović, Sanja
AU  - Vlahović, Milica
AU  - Dojčinović, Marina
AU  - Stević, Zoran
AU  - Volkov Husović, Tatjana
AU  - Bondarenko, Olexander
PY  - 2017
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/6917
AB  - Cavitation erosion of mullite samples was monitored using vibratory cavitation set up with stationary sample. The level of degradation of the sample was monitored using weight loss and image analysis. Thermal imaging analysis was focused on determination of temperature line profile and histogram of temperature distribution at the end of the experiment. The results of image analysis were compared with infrared thermography results.
PB  - ПП Полiтexперiодика
C3  - Proceedings - XVIII International scientific-practical conference, Modern information and electronic technologies
T1  - Implementation of infrared thermography on defects monitoring during cavitation erosion of mullite ceramic
SP  - 48
EP  - 51
UR  - https://hdl.handle.net/21.15107/rcub_cer_6917
ER  - 

@conference{
author = "Pavlović, Marko and Martinović, Sanja and Vlahović, Milica and Dojčinović, Marina and Stević, Zoran and Volkov Husović, Tatjana and Bondarenko, Olexander",
year = "2017",
abstract = "Cavitation erosion of mullite samples was monitored using vibratory cavitation set up with stationary sample. The level of degradation of the sample was monitored using weight loss and image analysis. Thermal imaging analysis was focused on determination of temperature line profile and histogram of temperature distribution at the end of the experiment. The results of image analysis were compared with infrared thermography results.",
publisher = "ПП Полiтexперiодика",
journal = "Proceedings - XVIII International scientific-practical conference, Modern information and electronic technologies",
title = "Implementation of infrared thermography on defects monitoring during cavitation erosion of mullite ceramic",
pages = "48-51",
url = "https://hdl.handle.net/21.15107/rcub_cer_6917"
}

Pavlović, M., Martinović, S., Vlahović, M., Dojčinović, M., Stević, Z., Volkov Husović, T.,& Bondarenko, O.. (2017). Implementation of infrared thermography on defects monitoring during cavitation erosion of mullite ceramic. in Proceedings - XVIII International scientific-practical conference, Modern information and electronic technologies
ПП Полiтexперiодика., 48-51.
https://hdl.handle.net/21.15107/rcub_cer_6917

Pavlović M, Martinović S, Vlahović M, Dojčinović M, Stević Z, Volkov Husović T, Bondarenko O. Implementation of infrared thermography on defects monitoring during cavitation erosion of mullite ceramic. in Proceedings - XVIII International scientific-practical conference, Modern information and electronic technologies. 2017;:48-51.
https://hdl.handle.net/21.15107/rcub_cer_6917 .

Pavlović, Marko, Martinović, Sanja, Vlahović, Milica, Dojčinović, Marina, Stević, Zoran, Volkov Husović, Tatjana, Bondarenko, Olexander, "Implementation of infrared thermography on defects monitoring during cavitation erosion of mullite ceramic" in Proceedings - XVIII International scientific-practical conference, Modern information and electronic technologies (2017):48-51,
https://hdl.handle.net/21.15107/rcub_cer_6917 .

TY  - JOUR
AU  - Pavlović, Marko D.
AU  - Dojčinović, Marina
AU  - Martinović, Sanja
AU  - Vlahović, Milica
AU  - Stević, Zoran
AU  - Jovanović, Marina N.
AU  - Volkov-Husović, Tatjana
PY  - 2017
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/2056
AB  - Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation erosion testing. Mass loss was taken as a conventional criterion for material degradation, while the level of surface degradation was evaluated by image and thermal imaging analyses. Results show high cavitation resistance of zircon ceramics and their suitability when vigorous cavitation erosion environment is expected.
PB  - Belgrade : International Institute for the Science of Sintering
T2  - Science of Sintering
T1  - Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic
VL  - 49
IS  - 2
SP  - 175
EP  - 185
DO  - 10.2298/SOS1702175P
ER  - 

@article{
author = "Pavlović, Marko D. and Dojčinović, Marina and Martinović, Sanja and Vlahović, Milica and Stević, Zoran and Jovanović, Marina N. and Volkov-Husović, Tatjana",
year = "2017",
abstract = "Mechanical shock of zircon based ceramic induced by cavitation erosion testing was investigated in this study. Several parameters were followed in order to determine level of material degradation during the cavitation erosion testing. Mass loss was taken as a conventional criterion for material degradation, while the level of surface degradation was evaluated by image and thermal imaging analyses. Results show high cavitation resistance of zircon ceramics and their suitability when vigorous cavitation erosion environment is expected.",
publisher = "Belgrade : International Institute for the Science of Sintering",
journal = "Science of Sintering",
title = "Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic",
volume = "49",
number = "2",
pages = "175-185",
doi = "10.2298/SOS1702175P"
}

Pavlović, M. D., Dojčinović, M., Martinović, S., Vlahović, M., Stević, Z., Jovanović, M. N.,& Volkov-Husović, T.. (2017). Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic. in Science of Sintering
Belgrade : International Institute for the Science of Sintering., 49(2), 175-185.
https://doi.org/10.2298/SOS1702175P

Pavlović MD, Dojčinović M, Martinović S, Vlahović M, Stević Z, Jovanović MN, Volkov-Husović T. Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic. in Science of Sintering. 2017;49(2):175-185.
doi:10.2298/SOS1702175P .

Pavlović, Marko D., Dojčinović, Marina, Martinović, Sanja, Vlahović, Milica, Stević, Zoran, Jovanović, Marina N., Volkov-Husović, Tatjana, "Determination of Degradation Level during Cavitation Erosion of Zircon Based Ceramic" in Science of Sintering, 49, no. 2 (2017):175-185,
https://doi.org/10.2298/SOS1702175P . .

TY  - CONF
AU  - Pavlović, Marko
AU  - Dojčinović, Marina
AU  - Martinović, Sanja
AU  - Vlahović, Milica
AU  - Stević, Zoran
AU  - Volkov Husović, Tatjana
PY  - 2016
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/7257
AB  - The paper presents the results of testing the mullite ceramics in terms of cavitation erosion. Mullite samples were sintered at 1200 °C. To determine the cavitation resistance the ultrasonic vibration method with stationary specimen was used. Mass loss and level of degradation of surface samples were monitored using the image analysis. Test results showed a high cavitation resistance of mullite ceramics and its possible application to various areas-metallurgy, mining, construction, chemical industry, where it is expected the presence of cavitation erosion.
PB  - Bor : University of Belgrade - Technical Faculty in Bor
PB  - Bor : Mining and Metallurgy Institute Bor
C3  - The 48th International October Conference on Mining and Metallurgy, Proceedings, September 28 - October 1st, 2016, Bor, Serbia
T1  - Cavitation damage of mullite ceramic: implementation of image analysis
SP  - 241
EP  - 244
UR  - https://hdl.handle.net/21.15107/rcub_cer_7257
ER  - 

@conference{
author = "Pavlović, Marko and Dojčinović, Marina and Martinović, Sanja and Vlahović, Milica and Stević, Zoran and Volkov Husović, Tatjana",
year = "2016",
abstract = "The paper presents the results of testing the mullite ceramics in terms of cavitation erosion. Mullite samples were sintered at 1200 °C. To determine the cavitation resistance the ultrasonic vibration method with stationary specimen was used. Mass loss and level of degradation of surface samples were monitored using the image analysis. Test results showed a high cavitation resistance of mullite ceramics and its possible application to various areas-metallurgy, mining, construction, chemical industry, where it is expected the presence of cavitation erosion.",
publisher = "Bor : University of Belgrade - Technical Faculty in Bor, Bor : Mining and Metallurgy Institute Bor",
journal = "The 48th International October Conference on Mining and Metallurgy, Proceedings, September 28 - October 1st, 2016, Bor, Serbia",
title = "Cavitation damage of mullite ceramic: implementation of image analysis",
pages = "241-244",
url = "https://hdl.handle.net/21.15107/rcub_cer_7257"
}

Pavlović, M., Dojčinović, M., Martinović, S., Vlahović, M., Stević, Z.,& Volkov Husović, T.. (2016). Cavitation damage of mullite ceramic: implementation of image analysis. in The 48th International October Conference on Mining and Metallurgy, Proceedings, September 28 - October 1st, 2016, Bor, Serbia
Bor : University of Belgrade - Technical Faculty in Bor., 241-244.
https://hdl.handle.net/21.15107/rcub_cer_7257

Pavlović M, Dojčinović M, Martinović S, Vlahović M, Stević Z, Volkov Husović T. Cavitation damage of mullite ceramic: implementation of image analysis. in The 48th International October Conference on Mining and Metallurgy, Proceedings, September 28 - October 1st, 2016, Bor, Serbia. 2016;:241-244.
https://hdl.handle.net/21.15107/rcub_cer_7257 .

Pavlović, Marko, Dojčinović, Marina, Martinović, Sanja, Vlahović, Milica, Stević, Zoran, Volkov Husović, Tatjana, "Cavitation damage of mullite ceramic: implementation of image analysis" in The 48th International October Conference on Mining and Metallurgy, Proceedings, September 28 - October 1st, 2016, Bor, Serbia (2016):241-244,
https://hdl.handle.net/21.15107/rcub_cer_7257 .

TY  - JOUR
AU  - Pavlović, Marko
AU  - Dojčinović, Marina
AU  - Martinović, Sanja
AU  - Vlahović, Milica
AU  - Stević, Zoran
AU  - Volkov-Husović, Tatjana
PY  - 2016
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/1858
AB  - Coating materials are widely used in refractory lining to prevent different deleterious effects such are reactions on the mold-metal contact surface, abrasion from liquid metal or alloy, gasses, slags, and other materials in contact with the coating. In this paper, behavior of cordierite based coating exposed to the cavitation erosion was investigated. Cordierite samples sintered at 1200 and 1400 degrees C were used for the tests. Mass loss, level of surface degradation obtained using image analysis and thermal imaging analysis were applied for the cavitation erosion evaluation. Results showed that the cordierite samples can be successfully used in conditions where the cavitation resistance is required.
PB  - Elsevier
T2  - Composites Part B-Engineering
T1  - Non destructive monitoring of cavitation erosion of cordierite based coatings
VL  - 97
SP  - 84
EP  - 91
DO  - 10.1016/j.compositesb.2016.04.073
ER  - 

@article{
author = "Pavlović, Marko and Dojčinović, Marina and Martinović, Sanja and Vlahović, Milica and Stević, Zoran and Volkov-Husović, Tatjana",
year = "2016",
abstract = "Coating materials are widely used in refractory lining to prevent different deleterious effects such are reactions on the mold-metal contact surface, abrasion from liquid metal or alloy, gasses, slags, and other materials in contact with the coating. In this paper, behavior of cordierite based coating exposed to the cavitation erosion was investigated. Cordierite samples sintered at 1200 and 1400 degrees C were used for the tests. Mass loss, level of surface degradation obtained using image analysis and thermal imaging analysis were applied for the cavitation erosion evaluation. Results showed that the cordierite samples can be successfully used in conditions where the cavitation resistance is required.",
publisher = "Elsevier",
journal = "Composites Part B-Engineering",
title = "Non destructive monitoring of cavitation erosion of cordierite based coatings",
volume = "97",
pages = "84-91",
doi = "10.1016/j.compositesb.2016.04.073"
}

Pavlović, M., Dojčinović, M., Martinović, S., Vlahović, M., Stević, Z.,& Volkov-Husović, T.. (2016). Non destructive monitoring of cavitation erosion of cordierite based coatings. in Composites Part B-Engineering
Elsevier., 97, 84-91.
https://doi.org/10.1016/j.compositesb.2016.04.073

Pavlović M, Dojčinović M, Martinović S, Vlahović M, Stević Z, Volkov-Husović T. Non destructive monitoring of cavitation erosion of cordierite based coatings. in Composites Part B-Engineering. 2016;97:84-91.
doi:10.1016/j.compositesb.2016.04.073 .

Pavlović, Marko, Dojčinović, Marina, Martinović, Sanja, Vlahović, Milica, Stević, Zoran, Volkov-Husović, Tatjana, "Non destructive monitoring of cavitation erosion of cordierite based coatings" in Composites Part B-Engineering, 97 (2016):84-91,
https://doi.org/10.1016/j.compositesb.2016.04.073 . .

TY  - JOUR
AU  - Pavlović, Marko
AU  - Dojčinović, Marina
AU  - Martinović, Sanja
AU  - Vlahović, Milica
AU  - Stević, Zoran
AU  - Volkov-Husović, Tatjana
PY  - 2016
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/4309
AB  - Coating materials are widely used in refractory lining to prevent different deleterious effects such are reactions on the mold-metal contact surface, abrasion from liquid metal or alloy, gasses, slags, and other materials in contact with the coating. In this paper, behavior of cordierite based coating exposed to the cavitation erosion was investigated. Cordierite samples sintered at 1200 and 1400 degrees C were used for the tests. Mass loss, level of surface degradation obtained using image analysis and thermal imaging analysis were applied for the cavitation erosion evaluation. Results showed that the cordierite samples can be successfully used in conditions where the cavitation resistance is required.
PB  - Elsevier
T2  - Composites Part B-Engineering
T1  - Non destructive monitoring of cavitation erosion of cordierite based coatings
VL  - 97
SP  - 84
EP  - 91
DO  - 10.1016/j.compositesb.2016.04.073
ER  - 

@article{
author = "Pavlović, Marko and Dojčinović, Marina and Martinović, Sanja and Vlahović, Milica and Stević, Zoran and Volkov-Husović, Tatjana",
year = "2016",
abstract = "Coating materials are widely used in refractory lining to prevent different deleterious effects such are reactions on the mold-metal contact surface, abrasion from liquid metal or alloy, gasses, slags, and other materials in contact with the coating. In this paper, behavior of cordierite based coating exposed to the cavitation erosion was investigated. Cordierite samples sintered at 1200 and 1400 degrees C were used for the tests. Mass loss, level of surface degradation obtained using image analysis and thermal imaging analysis were applied for the cavitation erosion evaluation. Results showed that the cordierite samples can be successfully used in conditions where the cavitation resistance is required.",
publisher = "Elsevier",
journal = "Composites Part B-Engineering",
title = "Non destructive monitoring of cavitation erosion of cordierite based coatings",
volume = "97",
pages = "84-91",
doi = "10.1016/j.compositesb.2016.04.073"
}

Pavlović, M., Dojčinović, M., Martinović, S., Vlahović, M., Stević, Z.,& Volkov-Husović, T.. (2016). Non destructive monitoring of cavitation erosion of cordierite based coatings. in Composites Part B-Engineering
Elsevier., 97, 84-91.
https://doi.org/10.1016/j.compositesb.2016.04.073

Pavlović M, Dojčinović M, Martinović S, Vlahović M, Stević Z, Volkov-Husović T. Non destructive monitoring of cavitation erosion of cordierite based coatings. in Composites Part B-Engineering. 2016;97:84-91.
doi:10.1016/j.compositesb.2016.04.073 .

Pavlović, Marko, Dojčinović, Marina, Martinović, Sanja, Vlahović, Milica, Stević, Zoran, Volkov-Husović, Tatjana, "Non destructive monitoring of cavitation erosion of cordierite based coatings" in Composites Part B-Engineering, 97 (2016):84-91,
https://doi.org/10.1016/j.compositesb.2016.04.073 . .