@article{
author = "Radetić, Tamara and Popović, M. and Jegdić, Bore and Romhanji, E.",
year = "2016",
abstract = "Influence of annealing temperature on beta-(Al3Mg2) phase precipitation and corrosion properties of sensitised Al-6.8wt% Mg alloy is investigated. Sensitisation of specimens annealed at 320 degrees C results in IGC and SCC susceptibility. Microstructural characterization shows fine precipitation of Mg-rich phase forming nearly continuous film at grain boundaries, despite small precipitated fraction (0.5%), and grain boundary faceting. Sensitised specimens annealed at 265 degrees C are IGC susceptible, but SCC resistant. Precipitation at grain boundaries is discrete, although the precipitated fraction is greater (3%) than in specimens annealed at 320 degrees C. Potentiodynamic measurements show that of all measured parameters, charge density is in the strongest correlation with the NAMLT and SSRT results.",
publisher = "Wiley",
journal = "Materials and Corrosion-Werkstoffe Und Korrosion",
title = "Influence of annealing temperature on sensitisation behaviour and corrosion properties of an Al-6.8wt% Mg alloy",
volume = "67",
number = "8",
pages = "867-875",
doi = "10.1002/maco.201508709"
}