TY  - JOUR
AU  - Filipović, Suzana
AU  - Obradovic, Nina
AU  - Krstić, Jugoslav
AU  - Scepanovic, M.
AU  - Pavlović, Vladimir B.
AU  - Paunović, Vesna
AU  - Ristic, M. M.
PY  - 2013
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/1274
AB  - In this article the influence of ball miling process on structure of MgO-TiO2 system, as well as the electrical properties of samples after sintering, was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 min. The influence of mechanical activation and sintering on the lattice vibrational spectra was studied by Raman spectroscopy at room temperature. Structural investigations have been performed on produced powders. Nitrogen adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results have been obtained: specific surface area continuosly decreased up to 40 min of activation and increased after that, reaching its minimun value of 5.5 m(2)/g. The Raman spectra of activated powders have shown that anatase modes have been decreasing in intensity and broadening as the time of activation extended. Also, the additional modes attributed to TiO2 II, srilankite and rutile phases started to appear as a consequence of activation. The small differences noticed in the Raman spectra of sintered samples have been explained by structural modification of MgTiO3 phase due to the presence of defects. The effects of activation and sintering process on microstructure were investigated by scanning electron microscopy (SEM). The electrical measurements showed difference in dielectric constant (epsilon(r)), loss tangent (tg delta) and specific resistance (rho) as a function of time of mechanical treatment.
PB  - Elsevier
T2  - Journal of Alloys and Compounds
T1  - Structural characterization and electrical properties of sintered magnesium-titanate ceramics
VL  - 555
SP  - 39
EP  - 44
DO  - 10.1016/j.jallcom.2012.12.040
ER  - 

@article{
author = "Filipović, Suzana and Obradovic, Nina and Krstić, Jugoslav and Scepanovic, M. and Pavlović, Vladimir B. and Paunović, Vesna and Ristic, M. M.",
year = "2013",
abstract = "In this article the influence of ball miling process on structure of MgO-TiO2 system, as well as the electrical properties of samples after sintering, was investigated. The mixtures of MgO-TiO2 powders were mechanically activated in a planetary ball mill for the time period from 0 to 120 min. The influence of mechanical activation and sintering on the lattice vibrational spectra was studied by Raman spectroscopy at room temperature. Structural investigations have been performed on produced powders. Nitrogen adsorption method was used to determine the BET specific surface area and pore size distribution. Unusual results have been obtained: specific surface area continuosly decreased up to 40 min of activation and increased after that, reaching its minimun value of 5.5 m(2)/g. The Raman spectra of activated powders have shown that anatase modes have been decreasing in intensity and broadening as the time of activation extended. Also, the additional modes attributed to TiO2 II, srilankite and rutile phases started to appear as a consequence of activation. The small differences noticed in the Raman spectra of sintered samples have been explained by structural modification of MgTiO3 phase due to the presence of defects. The effects of activation and sintering process on microstructure were investigated by scanning electron microscopy (SEM). The electrical measurements showed difference in dielectric constant (epsilon(r)), loss tangent (tg delta) and specific resistance (rho) as a function of time of mechanical treatment.",
publisher = "Elsevier",
journal = "Journal of Alloys and Compounds",
title = "Structural characterization and electrical properties of sintered magnesium-titanate ceramics",
volume = "555",
pages = "39-44",
doi = "10.1016/j.jallcom.2012.12.040"
}

Filipović, S., Obradovic, N., Krstić, J., Scepanovic, M., Pavlović, V. B., Paunović, V.,& Ristic, M. M.. (2013). Structural characterization and electrical properties of sintered magnesium-titanate ceramics. in Journal of Alloys and Compounds
Elsevier., 555, 39-44.
https://doi.org/10.1016/j.jallcom.2012.12.040

Filipović S, Obradovic N, Krstić J, Scepanovic M, Pavlović VB, Paunović V, Ristic MM. Structural characterization and electrical properties of sintered magnesium-titanate ceramics. in Journal of Alloys and Compounds. 2013;555:39-44.
doi:10.1016/j.jallcom.2012.12.040 .

Filipović, Suzana, Obradovic, Nina, Krstić, Jugoslav, Scepanovic, M., Pavlović, Vladimir B., Paunović, Vesna, Ristic, M. M., "Structural characterization and electrical properties of sintered magnesium-titanate ceramics" in Journal of Alloys and Compounds, 555 (2013):39-44,
https://doi.org/10.1016/j.jallcom.2012.12.040 . .

TY  - JOUR
AU  - Pavlović, Vera P.
AU  - Krstić, Jugoslav
AU  - Scepanovic, M. J.
AU  - Dojčilović, Jablan R.
AU  - Minić, Dragica M.
AU  - Blanusa, J.
AU  - Stevanović, Suzana
AU  - Mitic, V.
AU  - Pavlović, Vladimir B.
PY  - 2011
UR  - https://cer.ihtm.bg.ac.rs/handle/123456789/808
AB  - In this article, in order to obtain tetragonal nanocrystalline BaTiO3, structural investigations of mechanically activated BaTiO3 powder have been performed. A mercury porosimetry analysis and scanning electron microscopy method have been applied for determination of the specific pore volume, porosity and microstructure morphology of the samples. The lattice vibration spectra of nonactivated and activated powders, their phase composition, lattice microstrains and the mean size of coherently diffracting domains were examined by Raman spectroscopy and the X-ray powder diffraction method. The average crystal structure of obtained nanocrystalline powders, estimated from X-ray diffraction data, gave evidence of retained, but slightly sustained tetragonality of powders, even for particles as small as similar to 30 nm. Raman spectroscopy also gave clear evidence for local tetragonal symmetries, in particular through the presence of a band at similar to 307 cm(-1).
PB  - Elsevier Sci Ltd, Oxford
T2  - Ceramics International
T1  - Structural investigation of mechanically activated nanocrystalline BaTiO3 powders
VL  - 37
IS  - 7
SP  - 2513
EP  - 2518
DO  - 10.1016/j.ceramint.2011.03.064
ER  - 

@article{
author = "Pavlović, Vera P. and Krstić, Jugoslav and Scepanovic, M. J. and Dojčilović, Jablan R. and Minić, Dragica M. and Blanusa, J. and Stevanović, Suzana and Mitic, V. and Pavlović, Vladimir B.",
year = "2011",
abstract = "In this article, in order to obtain tetragonal nanocrystalline BaTiO3, structural investigations of mechanically activated BaTiO3 powder have been performed. A mercury porosimetry analysis and scanning electron microscopy method have been applied for determination of the specific pore volume, porosity and microstructure morphology of the samples. The lattice vibration spectra of nonactivated and activated powders, their phase composition, lattice microstrains and the mean size of coherently diffracting domains were examined by Raman spectroscopy and the X-ray powder diffraction method. The average crystal structure of obtained nanocrystalline powders, estimated from X-ray diffraction data, gave evidence of retained, but slightly sustained tetragonality of powders, even for particles as small as similar to 30 nm. Raman spectroscopy also gave clear evidence for local tetragonal symmetries, in particular through the presence of a band at similar to 307 cm(-1).",
publisher = "Elsevier Sci Ltd, Oxford",
journal = "Ceramics International",
title = "Structural investigation of mechanically activated nanocrystalline BaTiO3 powders",
volume = "37",
number = "7",
pages = "2513-2518",
doi = "10.1016/j.ceramint.2011.03.064"
}

Pavlović, V. P., Krstić, J., Scepanovic, M. J., Dojčilović, J. R., Minić, D. M., Blanusa, J., Stevanović, S., Mitic, V.,& Pavlović, V. B.. (2011). Structural investigation of mechanically activated nanocrystalline BaTiO3 powders. in Ceramics International
Elsevier Sci Ltd, Oxford., 37(7), 2513-2518.
https://doi.org/10.1016/j.ceramint.2011.03.064

Pavlović VP, Krstić J, Scepanovic MJ, Dojčilović JR, Minić DM, Blanusa J, Stevanović S, Mitic V, Pavlović VB. Structural investigation of mechanically activated nanocrystalline BaTiO3 powders. in Ceramics International. 2011;37(7):2513-2518.
doi:10.1016/j.ceramint.2011.03.064 .

Pavlović, Vera P., Krstić, Jugoslav, Scepanovic, M. J., Dojčilović, Jablan R., Minić, Dragica M., Blanusa, J., Stevanović, Suzana, Mitic, V., Pavlović, Vladimir B., "Structural investigation of mechanically activated nanocrystalline BaTiO3 powders" in Ceramics International, 37, no. 7 (2011):2513-2518,
https://doi.org/10.1016/j.ceramint.2011.03.064 . .