AB  - This brief presents the transport parameters of silver layers on a polyimide substrate fabricated by an inkjet printing technology using nanoparticle inks with 20 wt% and 40 wt% silver. All the electrical characteristics of the samples were measured by Hall effect measurement system at 0.37 T. The electron mobility in inkjet printed silver layer was 7.07 and 4.58 cm(2)/V s for 20 wt% silver, 29.6 and 21.3 cm(2)/V s for 40 wt% silver at 77 and 300 K, respectively. The resistivity in inkjet printed silver layer with 20 wt% is 20.6 x 10(-6) and 27.1 x 10(-6) Omega cm, and 4.81 x 10(-6) and 8.27 x 10(-6) Omega cm for 40 wt% silver at 77 and 300 K, respectively. The surface morphology and profiles of the samples were obtained with an atomic force and scanning electron microscope.
PB  - Ieee-Inst Electrical Electronics Engineers Inc, Piscataway
T2  - IEEE Transactions on Electron Devices
T1  - Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures
VL  - 60
IS  - 9
SP  - 2963
EP  - 2967
DO  - 10.1109/TED.2013.2274661
ER  - 

@article{
author = "Menicanin, Aleksandar B. and Zivanov, Ljiljana D. and Stojanović, Goran M. and Samardzic, Natasa M. and Randjelović, Danijela",
year = "2013",
abstract = "This brief presents the transport parameters of silver layers on a polyimide substrate fabricated by an inkjet printing technology using nanoparticle inks with 20 wt% and 40 wt% silver. All the electrical characteristics of the samples were measured by Hall effect measurement system at 0.37 T. The electron mobility in inkjet printed silver layer was 7.07 and 4.58 cm(2)/V s for 20 wt% silver, 29.6 and 21.3 cm(2)/V s for 40 wt% silver at 77 and 300 K, respectively. The resistivity in inkjet printed silver layer with 20 wt% is 20.6 x 10(-6) and 27.1 x 10(-6) Omega cm, and 4.81 x 10(-6) and 8.27 x 10(-6) Omega cm for 40 wt% silver at 77 and 300 K, respectively. The surface morphology and profiles of the samples were obtained with an atomic force and scanning electron microscope.",
publisher = "Ieee-Inst Electrical Electronics Engineers Inc, Piscataway",
journal = "IEEE Transactions on Electron Devices",
title = "Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures",
volume = "60",
number = "9",
pages = "2963-2967",
doi = "10.1109/TED.2013.2274661"
}

Menicanin, A. B., Zivanov, L. D., Stojanović, G. M., Samardzic, N. M.,& Randjelović, D.. (2013). Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures. in IEEE Transactions on Electron Devices
Ieee-Inst Electrical Electronics Engineers Inc, Piscataway., 60(9), 2963-2967.
https://doi.org/10.1109/TED.2013.2274661

Menicanin AB, Zivanov LD, Stojanović GM, Samardzic NM, Randjelović D. Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures. in IEEE Transactions on Electron Devices. 2013;60(9):2963-2967.
doi:10.1109/TED.2013.2274661 .

Menicanin, Aleksandar B., Zivanov, Ljiljana D., Stojanović, Goran M., Samardzic, Natasa M., Randjelović, Danijela, "Transport Parameters of Inkjet Printed Nanoparticle Silver on Polyimide Substrate Measured at Room and Liquid Nitrogen Temperatures" in IEEE Transactions on Electron Devices, 60, no. 9 (2013):2963-2967,
https://doi.org/10.1109/TED.2013.2274661 . .