Oxygen reduction on a duplex stainless steel
Само за регистроване кориснике
1998
Чланак у часопису (Објављена верзија)
,
Elsevier
Метаподаци
Приказ свих података о документуАпстракт
O-2 reduction on duplex stainless steel was investigated in neutral and alkaline solutions with and without the presence of chloride ions. All polarization curves showed hysteresis with higher reaction rate in positive going sweep than in the negative one. Tafel slopes of about -90 mV dec(-1) in neutral and alkaline solutions without chloride ions and about -150 mV dec(-1) in NaCl solution were obtained. Reaction rate is almost independent on pH in solutions of pH lt 12 while in more alkaline solutions reaction order with respect to OH- ions of about -1 was obtained. Reaction rate and kinetic parameters for O-2 reduction on duplex stainless steel were compared to data for O-2 reduction on pure Fe and great similarity was found.
Кључне речи:
oxygen / stainless steel / reductionИзвор:
Corrosion Science, 1998, 40, 6, 849-860Издавач:
- Oxford : Pergamon-Elsevier Science Ltd
DOI: 10.1016/S0010-938X(98)00004-3
ISSN: 0010-938X
WoS: 000075260300001
Scopus: 2-s2.0-0032101435
Институција/група
IHTMTY - JOUR AU - Gojković, Snežana Lj. AU - Zečević, Strahinja K. AU - Obradović, Maja D. AU - Dražić, Dragutin M. PY - 1998 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/6342 AB - O-2 reduction on duplex stainless steel was investigated in neutral and alkaline solutions with and without the presence of chloride ions. All polarization curves showed hysteresis with higher reaction rate in positive going sweep than in the negative one. Tafel slopes of about -90 mV dec(-1) in neutral and alkaline solutions without chloride ions and about -150 mV dec(-1) in NaCl solution were obtained. Reaction rate is almost independent on pH in solutions of pH lt 12 while in more alkaline solutions reaction order with respect to OH- ions of about -1 was obtained. Reaction rate and kinetic parameters for O-2 reduction on duplex stainless steel were compared to data for O-2 reduction on pure Fe and great similarity was found. PB - Oxford : Pergamon-Elsevier Science Ltd T2 - Corrosion Science T1 - Oxygen reduction on a duplex stainless steel VL - 40 IS - 6 SP - 849 EP - 860 DO - 10.1016/S0010-938X(98)00004-3 ER -
@article{ author = "Gojković, Snežana Lj. and Zečević, Strahinja K. and Obradović, Maja D. and Dražić, Dragutin M.", year = "1998", abstract = "O-2 reduction on duplex stainless steel was investigated in neutral and alkaline solutions with and without the presence of chloride ions. All polarization curves showed hysteresis with higher reaction rate in positive going sweep than in the negative one. Tafel slopes of about -90 mV dec(-1) in neutral and alkaline solutions without chloride ions and about -150 mV dec(-1) in NaCl solution were obtained. Reaction rate is almost independent on pH in solutions of pH lt 12 while in more alkaline solutions reaction order with respect to OH- ions of about -1 was obtained. Reaction rate and kinetic parameters for O-2 reduction on duplex stainless steel were compared to data for O-2 reduction on pure Fe and great similarity was found.", publisher = "Oxford : Pergamon-Elsevier Science Ltd", journal = "Corrosion Science", title = "Oxygen reduction on a duplex stainless steel", volume = "40", number = "6", pages = "849-860", doi = "10.1016/S0010-938X(98)00004-3" }
Gojković, S. Lj., Zečević, S. K., Obradović, M. D.,& Dražić, D. M.. (1998). Oxygen reduction on a duplex stainless steel. in Corrosion Science Oxford : Pergamon-Elsevier Science Ltd., 40(6), 849-860. https://doi.org/10.1016/S0010-938X(98)00004-3
Gojković SL, Zečević SK, Obradović MD, Dražić DM. Oxygen reduction on a duplex stainless steel. in Corrosion Science. 1998;40(6):849-860. doi:10.1016/S0010-938X(98)00004-3 .
Gojković, Snežana Lj., Zečević, Strahinja K., Obradović, Maja D., Dražić, Dragutin M., "Oxygen reduction on a duplex stainless steel" in Corrosion Science, 40, no. 6 (1998):849-860, https://doi.org/10.1016/S0010-938X(98)00004-3 . .