Synthesis and characterization of Al pillared montmorillonite impregnated with cobalt
Autori
Marković, MarijaBanković, Predrag
Mudrinić, Tihana
Jović-Jovičić, Nataša
Ajduković, Marija
Milutinović Nikolić, Aleksandra
Marinović, Sanja
Konferencijski prilog (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Aluminum pillared clay (AP) was synthesized using ≤ 74 μm fraction of Na-exchanged clay from Wyoming, USA (Na-Wy). The process of pillaring was carried out according to a common procedure comprising the following steps: pillaring, rinsing, drying and calcination. The obtained pillared clay was impregnated with Co2+ using incipient wetness impregnation method. The obtained sample was calcined and denoted as CoAP. Powder X-ray diffraction (XRD) patterns of Na-Wy, AP and CoAP indicated the presence of montmorillonite, quartz and feldspar. The pillaring affected montmorillonite peak corresponding to the 001 reflection. The d001 value increased from 1.17 nm for Na-Wy to 1.82 nm for AP. The pillaring process also fixed the basal spacing and no swelling was registered. In the diffractogram of CoAP the 001 peak was not well defined and was shifted to higher 2theta values. Nitrogen adsorption–desorption isotherms were used to determine textural properties of the samples. Pillaring resulted in e...nhanced textural properties such as increased total pore volume and specific surface area in the mesoporous region, as well as increased micropore volume comparing with that of Na-Wy. On the other hand, for CoAP textural parameters’ values were lower than those of AP, which could be ascribed to successful cobalt impregnation.
Ključne reči:
aluminum pillared clay / cobalt impregnation / XRD / textural propertiesIzvor:
Program and book of abstracts - Serbian Ceramic Society Conference – Advanced Ceramics and Application VII, 17-19.09.2018, Belgrade, Serbia, 2018, 78-78Izdavač:
- Serbian Ceramic Society
Finansiranje / projekti:
- Nanostrukturni funkcionalni i kompozitni materijali u katalitičkim i sorpcionim procesima (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45001)
Institucija/grupa
IHTMTY - CONF AU - Marković, Marija AU - Banković, Predrag AU - Mudrinić, Tihana AU - Jović-Jovičić, Nataša AU - Ajduković, Marija AU - Milutinović Nikolić, Aleksandra AU - Marinović, Sanja PY - 2018 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/6324 AB - Aluminum pillared clay (AP) was synthesized using ≤ 74 μm fraction of Na-exchanged clay from Wyoming, USA (Na-Wy). The process of pillaring was carried out according to a common procedure comprising the following steps: pillaring, rinsing, drying and calcination. The obtained pillared clay was impregnated with Co2+ using incipient wetness impregnation method. The obtained sample was calcined and denoted as CoAP. Powder X-ray diffraction (XRD) patterns of Na-Wy, AP and CoAP indicated the presence of montmorillonite, quartz and feldspar. The pillaring affected montmorillonite peak corresponding to the 001 reflection. The d001 value increased from 1.17 nm for Na-Wy to 1.82 nm for AP. The pillaring process also fixed the basal spacing and no swelling was registered. In the diffractogram of CoAP the 001 peak was not well defined and was shifted to higher 2theta values. Nitrogen adsorption–desorption isotherms were used to determine textural properties of the samples. Pillaring resulted in enhanced textural properties such as increased total pore volume and specific surface area in the mesoporous region, as well as increased micropore volume comparing with that of Na-Wy. On the other hand, for CoAP textural parameters’ values were lower than those of AP, which could be ascribed to successful cobalt impregnation. PB - Serbian Ceramic Society C3 - Program and book of abstracts - Serbian Ceramic Society Conference – Advanced Ceramics and Application VII, 17-19.09.2018, Belgrade, Serbia T1 - Synthesis and characterization of Al pillared montmorillonite impregnated with cobalt SP - 78 EP - 78 UR - https://hdl.handle.net/21.15107/rcub_cer_6324 ER -
@conference{ author = "Marković, Marija and Banković, Predrag and Mudrinić, Tihana and Jović-Jovičić, Nataša and Ajduković, Marija and Milutinović Nikolić, Aleksandra and Marinović, Sanja", year = "2018", abstract = "Aluminum pillared clay (AP) was synthesized using ≤ 74 μm fraction of Na-exchanged clay from Wyoming, USA (Na-Wy). The process of pillaring was carried out according to a common procedure comprising the following steps: pillaring, rinsing, drying and calcination. The obtained pillared clay was impregnated with Co2+ using incipient wetness impregnation method. The obtained sample was calcined and denoted as CoAP. Powder X-ray diffraction (XRD) patterns of Na-Wy, AP and CoAP indicated the presence of montmorillonite, quartz and feldspar. The pillaring affected montmorillonite peak corresponding to the 001 reflection. The d001 value increased from 1.17 nm for Na-Wy to 1.82 nm for AP. The pillaring process also fixed the basal spacing and no swelling was registered. In the diffractogram of CoAP the 001 peak was not well defined and was shifted to higher 2theta values. Nitrogen adsorption–desorption isotherms were used to determine textural properties of the samples. Pillaring resulted in enhanced textural properties such as increased total pore volume and specific surface area in the mesoporous region, as well as increased micropore volume comparing with that of Na-Wy. On the other hand, for CoAP textural parameters’ values were lower than those of AP, which could be ascribed to successful cobalt impregnation.", publisher = "Serbian Ceramic Society", journal = "Program and book of abstracts - Serbian Ceramic Society Conference – Advanced Ceramics and Application VII, 17-19.09.2018, Belgrade, Serbia", title = "Synthesis and characterization of Al pillared montmorillonite impregnated with cobalt", pages = "78-78", url = "https://hdl.handle.net/21.15107/rcub_cer_6324" }
Marković, M., Banković, P., Mudrinić, T., Jović-Jovičić, N., Ajduković, M., Milutinović Nikolić, A.,& Marinović, S.. (2018). Synthesis and characterization of Al pillared montmorillonite impregnated with cobalt. in Program and book of abstracts - Serbian Ceramic Society Conference – Advanced Ceramics and Application VII, 17-19.09.2018, Belgrade, Serbia Serbian Ceramic Society., 78-78. https://hdl.handle.net/21.15107/rcub_cer_6324
Marković M, Banković P, Mudrinić T, Jović-Jovičić N, Ajduković M, Milutinović Nikolić A, Marinović S. Synthesis and characterization of Al pillared montmorillonite impregnated with cobalt. in Program and book of abstracts - Serbian Ceramic Society Conference – Advanced Ceramics and Application VII, 17-19.09.2018, Belgrade, Serbia. 2018;:78-78. https://hdl.handle.net/21.15107/rcub_cer_6324 .
Marković, Marija, Banković, Predrag, Mudrinić, Tihana, Jović-Jovičić, Nataša, Ajduković, Marija, Milutinović Nikolić, Aleksandra, Marinović, Sanja, "Synthesis and characterization of Al pillared montmorillonite impregnated with cobalt" in Program and book of abstracts - Serbian Ceramic Society Conference – Advanced Ceramics and Application VII, 17-19.09.2018, Belgrade, Serbia (2018):78-78, https://hdl.handle.net/21.15107/rcub_cer_6324 .