Thermomagnetic analysis of nanocrystalline Nd4.5Fe 77B18.5 alloy
2009
Autori
Talijan, Nadežda M.Ćosović, Vladan
Stajić-Trošić, Jasna
Grujić, Aleksandar
Žak, Tomas
Lee, Z.
Radmilović, V.
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
Changes in the phase composition and crystallite size of a rapid quenched Nd4.5Fe77B18.5 alloy, caused by thermomagnetic measurements (TM) have been studied using XRD methods of phase analysis, crystallite size and lattice microstrain determination. Structural changes in regard to optimal magnetic state were additionally analyzed by TEM. Magnetic properties in optimal magnetic state and after TM were observed using room temperature SQUID measurements. The obtained experimental results suggest the Fe3B/Nd2Fe14B and partly α-Fe nanocomposite structure of the alloy in the optimized magnetic state, with mean crystallite size (< 30 nm). After TM, an increased amount of α-Fe phase, presence of different oxide and Fe-B phases as well as growth of crystallites are found to be the main reasons for the observed quality loss of hard magnetic properties.
Ključne reči:
Low-neodymium neodymium-iron-boron alloy / Magnetic properties / Thermomagnetic measurements / X-ray diffractionIzvor:
Materials Transactions, 2009, 50, 9, 2302-2307Finansiranje / projekti:
- Dizajniranje nanokristalnih magnetnih materijala tipa (Nd,Pr)FeB i komponenti na bazi smart magnetnih materijala (RS-MESTD-MPN2006-2010-142035)
DOI: 10.2320/matertrans.M2009138
ISSN: 1345-9678
WoS: 000271242900030
Scopus: 2-s2.0-70350352443
Institucija/grupa
IHTMTY - JOUR AU - Talijan, Nadežda M. AU - Ćosović, Vladan AU - Stajić-Trošić, Jasna AU - Grujić, Aleksandar AU - Žak, Tomas AU - Lee, Z. AU - Radmilović, V. PY - 2009 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/617 AB - Changes in the phase composition and crystallite size of a rapid quenched Nd4.5Fe77B18.5 alloy, caused by thermomagnetic measurements (TM) have been studied using XRD methods of phase analysis, crystallite size and lattice microstrain determination. Structural changes in regard to optimal magnetic state were additionally analyzed by TEM. Magnetic properties in optimal magnetic state and after TM were observed using room temperature SQUID measurements. The obtained experimental results suggest the Fe3B/Nd2Fe14B and partly α-Fe nanocomposite structure of the alloy in the optimized magnetic state, with mean crystallite size (< 30 nm). After TM, an increased amount of α-Fe phase, presence of different oxide and Fe-B phases as well as growth of crystallites are found to be the main reasons for the observed quality loss of hard magnetic properties. T2 - Materials Transactions T1 - Thermomagnetic analysis of nanocrystalline Nd4.5Fe 77B18.5 alloy VL - 50 IS - 9 SP - 2302 EP - 2307 DO - 10.2320/matertrans.M2009138 ER -
@article{ author = "Talijan, Nadežda M. and Ćosović, Vladan and Stajić-Trošić, Jasna and Grujić, Aleksandar and Žak, Tomas and Lee, Z. and Radmilović, V.", year = "2009", abstract = "Changes in the phase composition and crystallite size of a rapid quenched Nd4.5Fe77B18.5 alloy, caused by thermomagnetic measurements (TM) have been studied using XRD methods of phase analysis, crystallite size and lattice microstrain determination. Structural changes in regard to optimal magnetic state were additionally analyzed by TEM. Magnetic properties in optimal magnetic state and after TM were observed using room temperature SQUID measurements. The obtained experimental results suggest the Fe3B/Nd2Fe14B and partly α-Fe nanocomposite structure of the alloy in the optimized magnetic state, with mean crystallite size (< 30 nm). After TM, an increased amount of α-Fe phase, presence of different oxide and Fe-B phases as well as growth of crystallites are found to be the main reasons for the observed quality loss of hard magnetic properties.", journal = "Materials Transactions", title = "Thermomagnetic analysis of nanocrystalline Nd4.5Fe 77B18.5 alloy", volume = "50", number = "9", pages = "2302-2307", doi = "10.2320/matertrans.M2009138" }
Talijan, N. M., Ćosović, V., Stajić-Trošić, J., Grujić, A., Žak, T., Lee, Z.,& Radmilović, V.. (2009). Thermomagnetic analysis of nanocrystalline Nd4.5Fe 77B18.5 alloy. in Materials Transactions, 50(9), 2302-2307. https://doi.org/10.2320/matertrans.M2009138
Talijan NM, Ćosović V, Stajić-Trošić J, Grujić A, Žak T, Lee Z, Radmilović V. Thermomagnetic analysis of nanocrystalline Nd4.5Fe 77B18.5 alloy. in Materials Transactions. 2009;50(9):2302-2307. doi:10.2320/matertrans.M2009138 .
Talijan, Nadežda M., Ćosović, Vladan, Stajić-Trošić, Jasna, Grujić, Aleksandar, Žak, Tomas, Lee, Z., Radmilović, V., "Thermomagnetic analysis of nanocrystalline Nd4.5Fe 77B18.5 alloy" in Materials Transactions, 50, no. 9 (2009):2302-2307, https://doi.org/10.2320/matertrans.M2009138 . .