Supramolecular Route to Well-Ordered Metal Nanofoams
Samo za registrovane korisnike
De, Hosson Jeff Th M.
ten, Brinke Gerrit
Članak u časopisu (Objavljena verzija)
MetapodaciPrikaz svih podataka o dokumentu
Metal nanofoams with a porosity above 50% v/v have recently attracted great. Interest In materials science due to their interesting properties.. We.. demonstrate a new straightforward route to prepare such nanofoams using diblock copolymer-based PS-block-P4VP-(PDP) supramolecules that self-assemble Into a bicontinuous gyroid morphology, consisting of PS network channels in a P4VP(PDP) matrix. After dissolving the PDP, the P4VP. collapses onto the PS struts and a free-standing bicontinuous. gyroid template of 50-100 mu m thickness and interconnected, uniformly sized pores Is formed. The hydrophilic P4VP corona facilitates the penetration of water-based plating reagents into the porous template and enables a successful metal deposition. After plating, the polymer is simply degraded by heating, resulting In a well-ordered inverse gyroid nickel-foam. Essential to this approach Is the removal of only one part of the matrix (i.e., PDP). Therefore, the template accounts for 50% v/v or more. T...he porosity characteristics (amount, size of pores) can be tuned by selecting the appropriate copolymer and by adjusting the amount of PDP.
Ključne reči:metal nanofoams / nanopores / diblock copolymers / supramolecules / metal plating
Izvor:ACS Nano, 2011, 5, 8, 6339-6348
- Amer Chemical Soc, Washington