Ispitivanje prianjanja fotopolimerizujućih akrilata ojačanih česticama MgAl- LDH@SiO2 na stomatološkoj hromiranoj leguri i na staklu

Abstract

Polimerne smole na bazi akrilata dobijene iz Bis-GMA (Bisfenol A glicidmetakrilat), koji je pogodan za fotopolimerizaciju, koriste se u stomatologiji za različite namene zbog lakoće nanošenja i mogućnosti da se utiče na njihova svojstva dodavanjem ojačanja različitog oblika i hemijskog sastava. Sintetisano je ojačanje u formi čestica na bazi dvostrukih slojevitih hidroksida magnezijuma i aluminijuma (MgAlLDH- Layered Double Hidroxides) nataloženih na silicijum dioksidu dobijenom iz ljuski pirinča. Kao podloge korišćene su metalna legura na bazi hroma i molibdena za primenu u stomatologiji i staklo u formi podloga za mikroskopske preparate. Adhezivna svojstva kompozita su bitna sa aspekta njihove primene. Adhezivna svojstva materijala su određena na osnovu merenja mikrotvrdoće kompozita i to primenom različitih opterećenja kako bi se procenio parametar adhezije koji pokazuje uticaj prevlake na podlogu. Upoređeno je kako se vezuje čista matrica od fotopolimerizujućeg akrilata sa podlogom od stomatološke legure sa vezivanjem za staklenu podlogu. Potom je upoređeno kako se vezuju kompozitni materijali na obe podloge. Adhezija je određena i na osnovu promene ugla kvašenja između kompozita i rezultati su upoređeni sa rezultatima mikroindentacije. Pokazalo se da dodatak kompozitnih čestica kao ojačanja u matricu od akrilata povećava adhezivna svojstva kompozita u odnosu na čistu matricu i da se ost

Polymer resins based on acrylates obtained from Bis-GMA (Bisphenol A glycide methacrylate), which is suitable for photopolymerization, are used in dentistry for various purposes due to the ease of application and the possibility to influence their properties by adding reinforcements of different shapes, crystal structure and chemical compositions. Reinforcement in the form of particles based on MgAlLDH (layered double hydroxide) deposited on silica obtained from rice husks on two substrates. A metal base and glass were used. The adhesive properties are important in order to see the possibility of using these materials in applications. In order to measure the adhesive properties of the material, the composite microhardness measurement method is used by applying different loads in order to evaluate the adhesion parameter that shows the effect of the coating on the substrate. It was compared to how a pure photopolymerizing acrylate matrix bonds with a chromium-based dental alloy substrate that is used in the production of different parts of dentures by bonding to a glass substrate. Then, it was compared how composite materials are bonded to both substrates. Adhesion was monitored through the change in wetting angle between the composites, and the results were compared with the results of microindentation. It was shown that the addition of composite particles increases the adhesive properties of the composite compared to the pure matrix and that better adhesion is achieved between the composite and the metal substrate than between the composite and the glass substrate.