dc.description.abstractThis paper addresses on investigation the possibility of electrolytic treatment the sulphur acidic waste solution, obtained in the conventional electrolytic copper refining process. Beside the high copper concentration, the high concentration of other metals, in this case nickel, is the main characteristic of these waste solutions. Due to this fact, the copper bearing anodes with non-standard nickel, lead, tin and antimony content were specially prepared for the refining process. Nickel content of all anodes was approximately 7.5 mass%, and the content of lead, tin and antimony was varied. The preliminary results, obtained using the standard electrochemical techniques, have indicated that the copper bearing anodes could be used under the same conditions as well as in the conventional copper refining process. The measurements in constant galvanostatic pulse have pointed out that the all chemical elements from copper bearing anodes were dissolved and only copper was deposited onto the cathode. It was also pointed out that Ni concentration in the base working electrolyte (sulphur acidic waste solution), after 72 h of process, increased to 102 mass% at T-1 = 63 +/- 2 degrees C and up to 122 mass% at T-1 = 73 +/- 2 degrees C, while arsenic concentration decreased to a minimum value.en
dc.publisherElsevier Science Bv, Amsterdam
dc.relationinfo:eu-repo/grantAgreement/MESTD/MPN2006-2010/142044/RS//
dc.rightsrestrictedAccess
dc.sourceJournal of Hazardous Materials
dc.subjectNon-standard copper bearing anodesen
dc.subjectElectrorefiningen
dc.subjectSulphur acidic waste solutionen
dc.subjectAlloying elementsen
dc.titleBehaviour of non-standard composition copper bearing anodes from the copper refining processen
dc.typearticle
dc.rights.licenseARR
dcterms.abstractСтајић Трошић, Јасна; Југовић, Бранимир З.; Гвозденовић, Милица М.; Стевановић, Јасмина; Јордовиц, Б.; Фриедрицх, Б.; Марковиц, Р.;
dc.citation.volume182
dc.citation.issue1-3
dc.citation.spage55
dc.citation.epage63
dc.citation.other182(1-3): 55-63
dc.citation.rankaM21
dc.identifier.pmid20667423
dc.identifier.doi10.1016/j.jhazmat.2010.05.137
dc.identifier.rcubConv_2556
dc.identifier.scopus2-s2.0-77955572578
dc.identifier.wos000282240800008
dc.type.versionpublishedVersion


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record