dc.description.abstractChanges in the phase composition and magnetic properties of three types of commercial Nd-Fe-B alloys with different Nd content - low (10-12 wt%), near stoichiometric (21-25 wt%) and rich (26-29 wt%) caused by thermomagnetic analysis (TM) were observed in regard to optimal magnetic state. Phase compositions of investigated alloys before and after TM measurement up to 800°C were compared using 57Fe Mössbauer spectroscopy and X-Ray analysis. The TM measurements decompose all three materials and the main products of decomposition process α-Fe and Fe2B phase. Observed changes in structure and phase composition had direct influence on magnetic properties. Loss of magnetic properties induced by thermal decomposition is clearly illustrated on corresponding SQUID hysteresis loops.en
dc.description.abstractIstraživane su promene faznog sastava i magnetnih svojstava u odnosu na optimalno magnetno stanje za tri tipa komercijalnih Nd-Fe-B legura sa različitim sadržajem neodijuma - niskim (10-12 mas %), bliskim stehiometrijskom (21-25 mas %) i visokim (26-29 mas %), prouzrokovanih termomagnetnim (TM) merenjima. Fazni sastavi istraživanih legura pre i posle TM merenja do 800°C su poređeni koršćenjem 57Fe Mössbauer spektroskopske fazne analize i rendgensko-difraktometrijske analize. Usled termomagnetnih merenja dolazi do dekompozicije sva tri istraživana materijala i kao osnovni produkti dekompozicije nastaju α-Fe i Fe2B faze. Posmatrane promene u strukturi i faznom sastavu imaju direktan uticaj na magnetna svojstva. Gubitak magnetnih svojstava nastao usled termičke dekompozicije je jasno ilustrovan odgovarajućim SQUID histerezisnim petljama.sr
dc.publisherInternational Institute for the Science of Sintering, Beograd
dc.relationinfo:eu-repo/grantAgreement/MESTD/MPN2006-2010/142035/RS//
dc.rightsopenAccess
dc.rights.urihttps://creativecommons.org/licenses/by/4.0/
dc.sourceScience of Sintering
dc.subjectNd-Fe-B alloysen
dc.subjectthermomagnetic measurementsen
dc.subjectphase compositionen
dc.subjectstructureen
dc.subjectmagnetic propertiesen
dc.subjectNd-Fe-B leguresr
dc.subjecttermomagnetna merenjasr
dc.subjectfazni sastavsr
dc.subjectstrukturasr
dc.subjectmagnetna svojstvasr
dc.titleA comparative thermomagnetic study of melt-spun Nd-Fe-B alloys with different Nd contenten
dc.typearticle
dc.rights.licenseBY
dcterms.abstractЗак, Т.; Грујић, Aлександар; Стајић Трошић, Јасна; Ћосовић, Владан; Талијан, Надежда М.;
dc.citation.volume41
dc.citation.issue3
dc.citation.spage337
dc.citation.epage345
dc.citation.other41(3): 337-345
dc.citation.rankM22
dc.identifier.doi10.2298/SOS0903337G
dc.identifier.fulltexthttps://cer.ihtm.bg.ac.rs//bitstream/id/9166/520.pdf
dc.identifier.scopus2-s2.0-76649140137
dc.identifier.wos000275835500012
dc.type.versionpublishedVersion


Документи

Thumbnail

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу