Differently shaped nanocrystalline (Fe, Y)3O4 and its adsorption efficiency toward inorganic arsenic species
Само за регистроване кориснике
2019
Аутори
Dojčinović, BiljanaJančar, Boštjan
Bessais, Lotfi
Kremenović, Aleksandar
Jović-Jovičić, Nataša
Banković, Predrag
Stanković, Dalibor
Ognjanović, Miloš
Antić, Bratislav
Чланак у часопису (Објављена верзија)
,
IOP Publishing
Метаподаци
Приказ свих података о документуАпстракт
Herein we report effects of partial substitution of Fe3+ by Y3+ in magnetite (Fe3O4) on morphology and inorganic arsenic species adsorption efficiency of the Fe3−x Y x O4 nanoparticles formed. The series of Fe3−x Y x O4 (x = 0.00, 0.042 and 0.084, labeled as Y00, Y05 and Y10, respectively) was synthesized using co-precipitation followed by microwave-hydrothermal treatment (MW) at 200 °C. With increase of yttrium content (x value), both the morphological inhomogeneity of the samples and the fraction of spinel nanorods as compared to spinel pseudospherical particles increased. By both transmission electron microscopy and x-ray powder diffraction analyses, it was determined that the direction of growth of the spinel nanorods is along the [110] crystallographic direction. The Fe3−x Y x O4 affinities of adsorption toward the inorganic arsenic species, As(III) (arsenite, AsO3 3−) and As(V) (arsenate, AsO4 3−), were investigated. Increased Y3+ content related to changes in sample morphology w...as followed by a decrease of As(III) removal efficiency and vice versa for As(V). The increase in Y3+ content, in addition to increasing the adsorption capacity for As(V), significantly expanded the optimum pH range for the maximum removal and decreased the contact time for necessary 50% removal (t 1/2) of As(V) (Y00: pH 2–3, t 1/2 = 3.12 min; Y05: pH 2–6, t 1/2 = 2.12 min and Y10: pH 2–10, t 1/2 = 1.12 min). The results point to incorporation of Y3+ in the crystal lattice of magnetite, inducing nanorod spinel structure formation with significant changes in sorption properties important for the removal of inorganic arsenic from waters.
Кључне речи:
microstructure / arsenic / microwave-hydrothermal synthesis / adsorption / magnetic nanoparticlesИзвор:
Nanotechnology, 2019, 30, 47, 475702-Издавач:
- IOP Publishing
Финансирање / пројекти:
- Strengthening of the MagBioVin Research and Innovation Team for Development of Novel Approaches for Tumour Therapy based on Nanostructured Materials (EU-FP7-621375)
- Ministry of Education, Science and Technological Development of the Republic of Serbia- Eureka Project, E!9982
- Магнетни и радионуклидима обележени наноструктурни материјали за примене у медицини (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45015)
- Примена унапређених оксидационих процеса и наноструктурисаних оксидних материјала за уклањање загађивача из животне средине, развој и оптимизација инструменталних техника за праћење ефикасности (RS-MESTD-Basic Research (BR or ON)-172030)
Напомена:
- The peer-reviewed version: http://cer.ihtm.bg.ac.rs/handle/123456789/3244
DOI: 10.1088/1361-6528/ab3ca2
ISSN: 0957-4484; 1361-6528
PubMed: 31426045
WoS: 000484737400002
Scopus: 2-s2.0-85074115311
Институција/група
IHTMTY - JOUR AU - Dojčinović, Biljana AU - Jančar, Boštjan AU - Bessais, Lotfi AU - Kremenović, Aleksandar AU - Jović-Jovičić, Nataša AU - Banković, Predrag AU - Stanković, Dalibor AU - Ognjanović, Miloš AU - Antić, Bratislav PY - 2019 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/3243 AB - Herein we report effects of partial substitution of Fe3+ by Y3+ in magnetite (Fe3O4) on morphology and inorganic arsenic species adsorption efficiency of the Fe3−x Y x O4 nanoparticles formed. The series of Fe3−x Y x O4 (x = 0.00, 0.042 and 0.084, labeled as Y00, Y05 and Y10, respectively) was synthesized using co-precipitation followed by microwave-hydrothermal treatment (MW) at 200 °C. With increase of yttrium content (x value), both the morphological inhomogeneity of the samples and the fraction of spinel nanorods as compared to spinel pseudospherical particles increased. By both transmission electron microscopy and x-ray powder diffraction analyses, it was determined that the direction of growth of the spinel nanorods is along the [110] crystallographic direction. The Fe3−x Y x O4 affinities of adsorption toward the inorganic arsenic species, As(III) (arsenite, AsO3 3−) and As(V) (arsenate, AsO4 3−), were investigated. Increased Y3+ content related to changes in sample morphology was followed by a decrease of As(III) removal efficiency and vice versa for As(V). The increase in Y3+ content, in addition to increasing the adsorption capacity for As(V), significantly expanded the optimum pH range for the maximum removal and decreased the contact time for necessary 50% removal (t 1/2) of As(V) (Y00: pH 2–3, t 1/2 = 3.12 min; Y05: pH 2–6, t 1/2 = 2.12 min and Y10: pH 2–10, t 1/2 = 1.12 min). The results point to incorporation of Y3+ in the crystal lattice of magnetite, inducing nanorod spinel structure formation with significant changes in sorption properties important for the removal of inorganic arsenic from waters. PB - IOP Publishing T2 - Nanotechnology T1 - Differently shaped nanocrystalline (Fe, Y)3O4 and its adsorption efficiency toward inorganic arsenic species VL - 30 IS - 47 SP - 475702 DO - 10.1088/1361-6528/ab3ca2 ER -
@article{ author = "Dojčinović, Biljana and Jančar, Boštjan and Bessais, Lotfi and Kremenović, Aleksandar and Jović-Jovičić, Nataša and Banković, Predrag and Stanković, Dalibor and Ognjanović, Miloš and Antić, Bratislav", year = "2019", abstract = "Herein we report effects of partial substitution of Fe3+ by Y3+ in magnetite (Fe3O4) on morphology and inorganic arsenic species adsorption efficiency of the Fe3−x Y x O4 nanoparticles formed. The series of Fe3−x Y x O4 (x = 0.00, 0.042 and 0.084, labeled as Y00, Y05 and Y10, respectively) was synthesized using co-precipitation followed by microwave-hydrothermal treatment (MW) at 200 °C. With increase of yttrium content (x value), both the morphological inhomogeneity of the samples and the fraction of spinel nanorods as compared to spinel pseudospherical particles increased. By both transmission electron microscopy and x-ray powder diffraction analyses, it was determined that the direction of growth of the spinel nanorods is along the [110] crystallographic direction. The Fe3−x Y x O4 affinities of adsorption toward the inorganic arsenic species, As(III) (arsenite, AsO3 3−) and As(V) (arsenate, AsO4 3−), were investigated. Increased Y3+ content related to changes in sample morphology was followed by a decrease of As(III) removal efficiency and vice versa for As(V). The increase in Y3+ content, in addition to increasing the adsorption capacity for As(V), significantly expanded the optimum pH range for the maximum removal and decreased the contact time for necessary 50% removal (t 1/2) of As(V) (Y00: pH 2–3, t 1/2 = 3.12 min; Y05: pH 2–6, t 1/2 = 2.12 min and Y10: pH 2–10, t 1/2 = 1.12 min). The results point to incorporation of Y3+ in the crystal lattice of magnetite, inducing nanorod spinel structure formation with significant changes in sorption properties important for the removal of inorganic arsenic from waters.", publisher = "IOP Publishing", journal = "Nanotechnology", title = "Differently shaped nanocrystalline (Fe, Y)3O4 and its adsorption efficiency toward inorganic arsenic species", volume = "30", number = "47", pages = "475702", doi = "10.1088/1361-6528/ab3ca2" }
Dojčinović, B., Jančar, B., Bessais, L., Kremenović, A., Jović-Jovičić, N., Banković, P., Stanković, D., Ognjanović, M.,& Antić, B.. (2019). Differently shaped nanocrystalline (Fe, Y)3O4 and its adsorption efficiency toward inorganic arsenic species. in Nanotechnology IOP Publishing., 30(47), 475702. https://doi.org/10.1088/1361-6528/ab3ca2
Dojčinović B, Jančar B, Bessais L, Kremenović A, Jović-Jovičić N, Banković P, Stanković D, Ognjanović M, Antić B. Differently shaped nanocrystalline (Fe, Y)3O4 and its adsorption efficiency toward inorganic arsenic species. in Nanotechnology. 2019;30(47):475702. doi:10.1088/1361-6528/ab3ca2 .
Dojčinović, Biljana, Jančar, Boštjan, Bessais, Lotfi, Kremenović, Aleksandar, Jović-Jovičić, Nataša, Banković, Predrag, Stanković, Dalibor, Ognjanović, Miloš, Antić, Bratislav, "Differently shaped nanocrystalline (Fe, Y)3O4 and its adsorption efficiency toward inorganic arsenic species" in Nanotechnology, 30, no. 47 (2019):475702, https://doi.org/10.1088/1361-6528/ab3ca2 . .