dc.creatorNikolić, Maria Vesna
dc.creatorVasiljević, Zorka
dc.creatorLuković, Miloljub
dc.creatorPavlović, Vera P.
dc.creatorVujancevic, J.
dc.creatorRadovanović, M.
dc.creatorKrstić, Jugoslav
dc.creatorVlahovic, B.
dc.creatorPavlović, Vladimir B.
dc.date.accessioned2019-01-30T18:00:02Z
dc.date.available2019-01-30T18:00:02Z
dc.date.issued2018
dc.identifier.issn0925-4005
dc.identifier.urihttps://cer.ihtm.bg.ac.rs/handle/123456789/2414
dc.description.abstractPseudobrookite based nanopowder was obtained by solid state synthesis of starting hematite and anatase nanopowders in the weight ratio 55:45. Structural and morphological properties were analyzed using X-ray diffraction (XRD), BET, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, UV/Vis diffuse reflectance spectroscopy, Field emission scanning electron microscopy (FESEM) and Transmission electron microscopy (TEM) confirming the formation of nanocrystalline pseudobrookite. The obtained powder was mixed with a binder (ethyl cellulose), dispersant (α-terpinol) and adhesion agents (acetic acid and distilled water) to obtain a thick film paste. It was screen printed on alumina substrate with interdigitated PdAg electrodes and fired at 600 °C for 30 min. Formation of a porous nanocrystalline thick film structure was shown using Scanning electron microscopy (SEM), while Hall measurements enabled determination of carrier mobility. Change of impedance response in the frequency range 42 Hz–1 MHz with humidity was analyzed at room temperature (25 °C) and 50 °C in the relative humidity range 30–90% and 40–90%, respectively. At 42 Hz, and room temperature the impedance reduced ∼28 times, while at 50 °C it reduced ∼147 times in the relative humidity range 40–90%. The sensor showed rapid response (16 s) and relatively low hysteresis (8.39% at 25 °C and 2.64% at 50 °C) showing that this is a promising material for application in humidity sensing.en
dc.publisherElsevier
dc.relationinfo:eu-repo/grantAgreement/MESTD/Integrated and Interdisciplinary Research (IIR or III)/45007/RS//
dc.relationinfo:eu-repo/grantAgreement/MESTD/Integrated and Interdisciplinary Research (IIR or III)/45014/RS//
dc.rightsrestrictedAccess
dc.sourceSensors and Actuators, B: Chemical
dc.subjectFe2TiO5en
dc.subjectHumidity sensoren
dc.subjectPseudobrookiteen
dc.subjectThick filmen
dc.titleHumidity sensing properties of nanocrystalline pseudobrookite (Fe2TiO5) based thick filmsen
dc.typearticle
dc.rights.licenseARR
dcterms.abstractВујанцевиц, Ј.; Радовановић, М.; Николић, Мариа Весна; Васиљевиц, З.З.; Влаховиц, Б.; Луковиц, М.Д.; Павловић, Владимир. Б.; Павловић, Вера П.; Крстић, Југослав;
dc.citation.volume277
dc.citation.spage654
dc.citation.epage664
dc.citation.other277: 654-664
dc.citation.rankaM21
dc.description.otherThe peer-reviewed version: [https://cer.ihtm.bg.ac.rs/handle/123456789/4277]
dc.identifier.doi10.1016/j.snb.2018.09.063
dc.identifier.scopus2-s2.0-85053789141
dc.identifier.wos000453066700081
dc.type.versionpublishedVersion


Документи

Thumbnail

Овај документ се појављује у следећим колекцијама

Приказ основних података о документу