Phenomenology of a formation of a honeycomb-like structure during copper electrodeposition
(Journal of Solid State Electrochemistry, 2007)
In this paper, the phenomenology of a formation of a honeycomb-like structure was considered. Copper deposits obtained at overpotential of 1000 mV were examined by scanning electron microscopy (SEM) technique. It was shown ...
Strukturne karakteristike galvanskih prevlaka bakra / Structural characteristics of electrodeposited copper coatings
(Bosnia and Herzegovina : University of East Sarajevo, Faculty of Technology, 2009)
Uzorci bakra su podvrgnuti mehaničkom i elektrohemijskom glačanju u odgovarajućim elektrolitima za elektrohemijsko glačanje. Na tako prethodno pripremljene površine supstrata izvršeno je taloţenje prevlaka bakra iz dva ...
Determination of critical conditions for the formation of electrodeposited copper structures suitable for electrodes in electrochemical devices
(MDPI, 2007)
Electrodeposition of copper from acid sulfate solutions at overpotentials on the plateau of the limiting diffusion current density and at higher overpotentials was examined. The average current efficiencies for hydrogen ...
The effects of the pause to pulse ratio in the regime of pulsating overpotential on the formation of honeycomb-like structures
(Elsevier Science Inc, New York, 2009)
The formation of honeycomb-like structures in the pulsating overpotential (PO) regime was examined by scanning electron microscopy (SEM). The honeycomb-like structures obtained with a square-wave PO of different pause to ...
Morphologies of copper deposits obtained by the electrodeposition at high overpotentials
(Elsevier, 2006)
Morphologies of copper deposits obtained at overpotentials belonging to the plateau of the limiting diffusion current density and at higher
overpotentials were examined by the scanning electron microscopy (SEM) technique. ...
Reflection and structural analyses of mirror-bright metal coatings
(Springer, 2004)
Reflection and structural analyses of different copper and zinc coatings were performed. The copper coatings were electrodeposited from a sulfate solution in the presence of thiourea, as well as in the presence of modified ...
Comparative reflection and structural analyses of copper and zinc coatings electrodeposited from acid sulfate solutions without and with additives
(Elsevier, 2002)
Reflection and structural analyses of different copper and zinc coatings were performed. The coatings of copper obtained were from acid sulfate solutions in the absence and presence of thiourea. The coatings of zinc were ...
Influence of potential pulse conditions on the formation of honeycomb-like copper electrodes
(Elsevier, 2009)
Electrodeposition of copper by pulsating overpotential (PO) regime in the hydrogen co-deposition range was examined by the determination of the average current efficiency of hydrogen evolution and by microscopic analysis ...
Formation of dish-like holes and a channel structure in electrodeposition of copper under hydrogen co-deposition
(Elsevier, 2007)
Copper electrodeposition from acid sulfate solutions at an overpotential of 1000 mV, which is about 250 mV outside the plateau of the limiting diffusion current density, was examined by the determination of the average ...
Influence of the magnetic field and magnetoresistance on the electrodeposition of Ni nanocontacts in thin films and microwires
(Elsevier, 2004)
We present a study of electrodeposition of Ni nanocontacts in thin film and microwires gaps under an external applied magnetic field. The study is performed in comparison with electrodeposition of Cu that is not a magnetic ...