Direct electroplating of copper coatings onto aluminum / Neposredno elektrohemijsko taloženje prevlaka bakra na aluminijum
(Belgrade, Serbia : Engineering Society for Corrosion, 2005)
The deposition of copper coatings has been done by direct electrochemical deposition from the solution: CuSO4 (55 g/dm3) + CH2 NH2 - CH2OH (100 g/dm3) + (NH4)2SO4 (30 g/dm3) + Na2SO4*10H2O (75 g/dm3) + Na2CO3 (3 g/dm3), ...
The effect of metal surface condition on the brightness and the structure of metal coatings. PART II, Morphology and structure of electrodeposited metal coatigs / Uticaj stanja površine metala na sjaj i strukturu metalnih prevlaka. II deo, Morfologija i struktura elektrohemijski istaloženih prevlaka metala
(Belgrade, Serbia : Engineering Society for Corrosion, 2007)
The properties which determine whether the metal surface is mirror bright are precisely determined by STM investigations. Mirror brightness of metal surfaces can be associated with the high degree of mirror reflection which ...
Influence of the synthesis procedures on pt catalyst activity for ethanol electrooxidation reaction / Uticaj postupka sinteze na aktivnost platinskih katalizatora za reakciju elektrooksidacije etanola
(Belgrade, Serbia : Engineering Society for Corrosion, 2016)
Carbon supported platinum catalysts for ethanol electrooxidation were synthesized by modified polyol synthesis method, assisted by microwave or reflux heating. Synthesized catalysts were characterized by XRD, STM and TGA ...
Influence of welding current intensity on pitting corrosion resistance in welded joint of stainless steel X5CrNi18-10 / Uticaj jačine struje zavarivanja na otpornost prema piting koroziji zavarenog spoja nerđajućeg čelika X5CrNi18-10
(Belgrade, Serbia : Engineering Society for Corrosion, 2017)
The effect of welding current on the pitting corrosion resistance in the welded joint of austenitic stainless steel X5CrNi18-10 was tested. Welding was carried out using three different current intensity (110 A, 130 A and ...
Correlation between crystal orientation and morphology of electrolytically produced powder particles: Analysis of the limiting cases / Korelacija izmedju orijentacije kristala i morfologije elektrolitički proizvedenih praškastih čestica - analiza graničnih slučajeva
(Belgrade, Serbia : Engineering Society for Corrosion, 2018)
Lead and nickel powder particles were produced by the processes of electrolysis and characterized by scanning electron microscope (SEM). The X-ray diffraction (XRD) analysis of the produced particles was done. Morphologies ...
The effect of preparation of aluminum surface on surface roughness / Uticaj pripreme površine aluminijuma na površinsku hrapavost
(Belgrade, Serbia : Engineering Society for Corrosion, 2004)
Aluminum samples were electrochemically polished in one of three solutions for electrochemical polishing. On those samples the surface roughness was measured. The effect of the anode treatment on surface roughness was also ...
The effect of preparation of aluminum surface on surface reflection / Uticaj pripreme površine aluminijuma na površinsku refleksiju
(Belgrade, Serbia : Engineering Society for Corrosion, 2004)
Aluminum samples were electrochemically polished in one of three solutions for electrochemical polishing. On those samples the surface reflection was measured. The effect of the anode treatment as the interface between the ...
Electroplating of silver onto aluminum and its alloys / Elektrohemijsko taloženje prevlaka srebra na aluminijum i njegove legure
(Belgrade, Serbia : Engineering Society for Corrosion, 2005)
In this paper the structural characteristics of silver coatings electrodeposited as final coatings onto aluminum were shown. The copper coating was electrodeposited as a basic coating directly onto aluminum. Afterward, ...
The effect of deposition time on the structure of the top coating of nickel electrodeposited onto aluminum / Uticaj vremena taloženja na strukturu završne prevlake nikla na aluminijumu
(Belgrade, Serbia : Engineering Society for Corrosion, 2004)
The microstructure of the chemical coating of zinc on aluminum, as well as electrodeposited nickel coating on chemically deposited zinc were investigated with change of one parameter only-deposition time. Based on the ...
The effect of preparation of aluminum surface on the structure of final coating of nickel / Uticaj pripreme površine aluminijuma na strukturu završne prevlake nikla
(Belgrade, Serbia : Engineering Society for Corrosion, 2003)
In this work structure characteristics of the final coating of nickel were studied. Nickel was deposited onto chemically prepared aluminum, chemically and electrochemically. Structural characteristics of metallic coatings ...