Anisotropy Analysis of Low Cement Concrete by Ultrasonic Measurements and Image Analysis
Članak u časopisu (Objavljena verzija)
MetapodaciPrikaz svih podataka o dokumentu
The analized material was high alumina low cement castable sintered at three different temperatures. Influence of initial material anisotropy on the thermal shock resistance as well as changes of anisotropy level during the thermal shock were studied. Water quench test was used as an experimental method for the thermal stability testing. Surface anisotropy was analysed by image analysis and structural anisotropy using ultrasonic measurements. The results pointed out that the highest homogeinity and the lowest surface and structural anisotropy was for the samples sintered at 1600 degrees C. Surface anistoropy had prevailing infuence on behavior of material during the thermal shock, but the structural anisotropy should not be neglected.
Ključne reči:Refractories / Anisotropy / Image analysis / Ultrasonic measurements / Low cement concrete
Izvor:Science of Sintering, 2016, 48, 1, 57-70
- International Institute for the Science of Sintering, Beograd