Structural, mechanical and tribological characterization of Zn25Al alloys with Si and Sr addition
Samo za registrovane korisnike
2014
Članak u časopisu (Objavljena verzija)
Metapodaci
Prikaz svih podataka o dokumentuApstrakt
The ZA-27 alloy is a zinc-aluminium casting alloy that has been frequently used as the material for sleeves of plain bearings. It has good physical, mechanical and tribological properties. However, one of the major disadvantages is its dimensional instability over a period of time (ageing). To overcome this, copper in the alloy may be replaced with silicon. Coarsening of silicon particles can be controlled by a suitable addition of strontium. In this paper, the commercial ZA-27 alloy and six different Zn25Al alloys (with 1 and 3 wt.% silicon; and with 0, 0.03 and 0.05 wt.% strontium) were obtained by casting in the pre-heated steel mould. Casting of the alloys was carried out at a laboratory level. In the alloys containing silicon, a finer dendritic structure was noticed compared to the structure of the commercial ZA-27 alloy. The addition of strontium influenced the size and distribution of primary silicon particles. Needle-like particles of eutectic silicon were changed into the fibr...ous ones. The presence of silicon and strontium did not significantly affect mechanical properties of the obtained Zn25Al alloys compared to mechanical properties of the commercial ZA-27 alloy. Wear rate of the alloys containing silicon was lower than that of the ZA-27 alloy. The addition of strontium further lowers the wear rate and slightly increases the coefficient of friction.
Ključne reči:
Zinc alloys / Strontium / Microstructure / Boundary lubrication / Friction / WearIzvor:
Materials & Design, 2014, 64, 381-392Izdavač:
- Elsevier Sci Ltd, Oxford
Finansiranje / projekti:
- Republic of Serbia, Ministry of Education, Science and Technological Development
- Uticaj nano i mikrostrukturnih konstituenata na sintezu i karakteristike savremenih kompozitnih materijala sa metalnom osnovom (RS-MESTD-Basic Research (BR or ON)-172005)
- Istraživanje i optimizacija tehnoloških i funkcionalnih performansi ventilacionog mlina termoelektrane Kostolac B (RS-MESTD-Technological Development (TD or TR)-34028)
- Razvoj triboloških mikro/nano dvokomponentnih i hibridnih samopodmazujućih kompozita (RS-MESTD-Technological Development (TD or TR)-35021)
DOI: 10.1016/j.matdes.2014.07.056
ISSN: 0261-3069
WoS: 000342681600050
Scopus: 2-s2.0-84908134802
Institucija/grupa
IHTMTY - JOUR AU - Vencl, Aleksandar AU - Bobić, Ilija AU - Vučetić, Filip AU - Bobić, Biljana AU - Ružić, Jovana PY - 2014 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/1399 AB - The ZA-27 alloy is a zinc-aluminium casting alloy that has been frequently used as the material for sleeves of plain bearings. It has good physical, mechanical and tribological properties. However, one of the major disadvantages is its dimensional instability over a period of time (ageing). To overcome this, copper in the alloy may be replaced with silicon. Coarsening of silicon particles can be controlled by a suitable addition of strontium. In this paper, the commercial ZA-27 alloy and six different Zn25Al alloys (with 1 and 3 wt.% silicon; and with 0, 0.03 and 0.05 wt.% strontium) were obtained by casting in the pre-heated steel mould. Casting of the alloys was carried out at a laboratory level. In the alloys containing silicon, a finer dendritic structure was noticed compared to the structure of the commercial ZA-27 alloy. The addition of strontium influenced the size and distribution of primary silicon particles. Needle-like particles of eutectic silicon were changed into the fibrous ones. The presence of silicon and strontium did not significantly affect mechanical properties of the obtained Zn25Al alloys compared to mechanical properties of the commercial ZA-27 alloy. Wear rate of the alloys containing silicon was lower than that of the ZA-27 alloy. The addition of strontium further lowers the wear rate and slightly increases the coefficient of friction. PB - Elsevier Sci Ltd, Oxford T2 - Materials & Design T1 - Structural, mechanical and tribological characterization of Zn25Al alloys with Si and Sr addition VL - 64 SP - 381 EP - 392 DO - 10.1016/j.matdes.2014.07.056 ER -
@article{ author = "Vencl, Aleksandar and Bobić, Ilija and Vučetić, Filip and Bobić, Biljana and Ružić, Jovana", year = "2014", abstract = "The ZA-27 alloy is a zinc-aluminium casting alloy that has been frequently used as the material for sleeves of plain bearings. It has good physical, mechanical and tribological properties. However, one of the major disadvantages is its dimensional instability over a period of time (ageing). To overcome this, copper in the alloy may be replaced with silicon. Coarsening of silicon particles can be controlled by a suitable addition of strontium. In this paper, the commercial ZA-27 alloy and six different Zn25Al alloys (with 1 and 3 wt.% silicon; and with 0, 0.03 and 0.05 wt.% strontium) were obtained by casting in the pre-heated steel mould. Casting of the alloys was carried out at a laboratory level. In the alloys containing silicon, a finer dendritic structure was noticed compared to the structure of the commercial ZA-27 alloy. The addition of strontium influenced the size and distribution of primary silicon particles. Needle-like particles of eutectic silicon were changed into the fibrous ones. The presence of silicon and strontium did not significantly affect mechanical properties of the obtained Zn25Al alloys compared to mechanical properties of the commercial ZA-27 alloy. Wear rate of the alloys containing silicon was lower than that of the ZA-27 alloy. The addition of strontium further lowers the wear rate and slightly increases the coefficient of friction.", publisher = "Elsevier Sci Ltd, Oxford", journal = "Materials & Design", title = "Structural, mechanical and tribological characterization of Zn25Al alloys with Si and Sr addition", volume = "64", pages = "381-392", doi = "10.1016/j.matdes.2014.07.056" }
Vencl, A., Bobić, I., Vučetić, F., Bobić, B.,& Ružić, J.. (2014). Structural, mechanical and tribological characterization of Zn25Al alloys with Si and Sr addition. in Materials & Design Elsevier Sci Ltd, Oxford., 64, 381-392. https://doi.org/10.1016/j.matdes.2014.07.056
Vencl A, Bobić I, Vučetić F, Bobić B, Ružić J. Structural, mechanical and tribological characterization of Zn25Al alloys with Si and Sr addition. in Materials & Design. 2014;64:381-392. doi:10.1016/j.matdes.2014.07.056 .
Vencl, Aleksandar, Bobić, Ilija, Vučetić, Filip, Bobić, Biljana, Ružić, Jovana, "Structural, mechanical and tribological characterization of Zn25Al alloys with Si and Sr addition" in Materials & Design, 64 (2014):381-392, https://doi.org/10.1016/j.matdes.2014.07.056 . .