The study of Zn-Co alloy coatings electrochemically deposited by pulse current
Ispitivanje prevlaka Zn-Co legura dobijenih pulsirajućom strujom
Апстракт
The electrochemical deposition by pulse current of Zn-Co alloy coatings on steel was examined, with the aim to find out whether pulse plating could produce alloys that could offer a better corrosion protection. The influence of on-time and the average current density on the cathodic current efficiency, coating morphology, surface roughness and corrosion stability in 3% NaCl was examined. At the same Ton/Toff ratio the current efficiency was insignificantly smaller for deposition at higher average current density. It was shown that, depending on the on-time, pulse plating could produce more homogenous alloy coatings with finer morphology, as compared to deposits obtained by direct current. The surface roughness was the greatest for Zn-Co alloy coatings deposited with direct current, as compared with alloy coatings deposited with pulse current, for both examined average current densities. It was also shown that Zn-Co alloy coatings deposited by pulse current could increase the corrosion ...stability of Zn-Co alloy coatings on steel. Namely, alloy coatings deposited with pulse current showed higher corrosion stability, as compared with alloy coatings deposited with direct current, for almost all examined cathodic times, Ton. Alloy coatings deposited at higher average current density showed greater corrosion stability as compared with coatings deposited by pulse current at smaller average current density. It was shown that deposits obtained with pulse current and cathodic time of 10 ms had the poorest corrosion stability, for both investigated average deposition current density. Among all investigated alloy coatings the highest corrosion stability was obtained for Zn-Co alloy coatings deposited with pulsed current at higher average current density (jav = 4 A dm-2).
Ispitivano je elektrohemijsko taloženje cink-kobalt legure pulsirajućom strujom na čeliku, a s ciljem dobijanja zaštitnih prevlaka sa povećanom korozionom stabilnošću. Prevlake legura su taložene pulsirajućim režimom sa različitim srednjim gustinama struje i pri različitom trajanju katodnog pulsa. Analiziran je uticaj ovih parametara na iskorišćenje struje prilikom elektrohemijskog taloženja na izgled prevlaka (snimanje elektronskim mikroskopom), hrapavost prevlaka i njihovu korozionu stabilnost u 3% NaCl (merenjem slobodnog korozionog potencijala u agensu korozije i snimanjem polarizacionih krivih). Pokazano je da u zavisnosti od vremena pulsa, prevlake taložene pulsirajućim režimom mogu da imaju bolju homogenost, sitnije aglomerate kristalnih zrna i manju hrapavost od onih taloženih pri istim uslovima, ali konstantnom gustinom struje. Veću korozionu stabilnost pokazale su prevlake legura taložene većom srednjom gustinom struje.
Кључне речи:
zinc-cobalt alloys / coatings / electrodeposition / pulse current / corrosion stability / Zn-Co legure / prevlake / elektrohemijsko taloženje / pulsirajuća struja / korozionastabilnostИзвор:
Hemijska industrija, 2012, 66, 5, 749-757Издавач:
- Association of Chemical Engineers of Serbia
Финансирање / пројекти:
- Синтеза, развој технологија добијања и примена наноструктурних мултифункционалних материјала дефинисаних својстава (RS-MESTD-Integrated and Interdisciplinary Research (IIR or III)-45019)
DOI: 10.2298/HEMIND111215035B
ISSN: 0367-598X
WoS: 000314735800016
Scopus: 2-s2.0-84869426300
Институција/група
IHTMTY - JOUR AU - Bajat, Jelena AU - Maksimović, Miodrag D. AU - Tomić, Milorad V. AU - Pavlović, Miomir PY - 2012 UR - https://cer.ihtm.bg.ac.rs/handle/123456789/1077 AB - The electrochemical deposition by pulse current of Zn-Co alloy coatings on steel was examined, with the aim to find out whether pulse plating could produce alloys that could offer a better corrosion protection. The influence of on-time and the average current density on the cathodic current efficiency, coating morphology, surface roughness and corrosion stability in 3% NaCl was examined. At the same Ton/Toff ratio the current efficiency was insignificantly smaller for deposition at higher average current density. It was shown that, depending on the on-time, pulse plating could produce more homogenous alloy coatings with finer morphology, as compared to deposits obtained by direct current. The surface roughness was the greatest for Zn-Co alloy coatings deposited with direct current, as compared with alloy coatings deposited with pulse current, for both examined average current densities. It was also shown that Zn-Co alloy coatings deposited by pulse current could increase the corrosion stability of Zn-Co alloy coatings on steel. Namely, alloy coatings deposited with pulse current showed higher corrosion stability, as compared with alloy coatings deposited with direct current, for almost all examined cathodic times, Ton. Alloy coatings deposited at higher average current density showed greater corrosion stability as compared with coatings deposited by pulse current at smaller average current density. It was shown that deposits obtained with pulse current and cathodic time of 10 ms had the poorest corrosion stability, for both investigated average deposition current density. Among all investigated alloy coatings the highest corrosion stability was obtained for Zn-Co alloy coatings deposited with pulsed current at higher average current density (jav = 4 A dm-2). AB - Ispitivano je elektrohemijsko taloženje cink-kobalt legure pulsirajućom strujom na čeliku, a s ciljem dobijanja zaštitnih prevlaka sa povećanom korozionom stabilnošću. Prevlake legura su taložene pulsirajućim režimom sa različitim srednjim gustinama struje i pri različitom trajanju katodnog pulsa. Analiziran je uticaj ovih parametara na iskorišćenje struje prilikom elektrohemijskog taloženja na izgled prevlaka (snimanje elektronskim mikroskopom), hrapavost prevlaka i njihovu korozionu stabilnost u 3% NaCl (merenjem slobodnog korozionog potencijala u agensu korozije i snimanjem polarizacionih krivih). Pokazano je da u zavisnosti od vremena pulsa, prevlake taložene pulsirajućim režimom mogu da imaju bolju homogenost, sitnije aglomerate kristalnih zrna i manju hrapavost od onih taloženih pri istim uslovima, ali konstantnom gustinom struje. Veću korozionu stabilnost pokazale su prevlake legura taložene većom srednjom gustinom struje. PB - Association of Chemical Engineers of Serbia T2 - Hemijska industrija T1 - The study of Zn-Co alloy coatings electrochemically deposited by pulse current T1 - Ispitivanje prevlaka Zn-Co legura dobijenih pulsirajućom strujom VL - 66 IS - 5 SP - 749 EP - 757 DO - 10.2298/HEMIND111215035B ER -
@article{ author = "Bajat, Jelena and Maksimović, Miodrag D. and Tomić, Milorad V. and Pavlović, Miomir", year = "2012", abstract = "The electrochemical deposition by pulse current of Zn-Co alloy coatings on steel was examined, with the aim to find out whether pulse plating could produce alloys that could offer a better corrosion protection. The influence of on-time and the average current density on the cathodic current efficiency, coating morphology, surface roughness and corrosion stability in 3% NaCl was examined. At the same Ton/Toff ratio the current efficiency was insignificantly smaller for deposition at higher average current density. It was shown that, depending on the on-time, pulse plating could produce more homogenous alloy coatings with finer morphology, as compared to deposits obtained by direct current. The surface roughness was the greatest for Zn-Co alloy coatings deposited with direct current, as compared with alloy coatings deposited with pulse current, for both examined average current densities. It was also shown that Zn-Co alloy coatings deposited by pulse current could increase the corrosion stability of Zn-Co alloy coatings on steel. Namely, alloy coatings deposited with pulse current showed higher corrosion stability, as compared with alloy coatings deposited with direct current, for almost all examined cathodic times, Ton. Alloy coatings deposited at higher average current density showed greater corrosion stability as compared with coatings deposited by pulse current at smaller average current density. It was shown that deposits obtained with pulse current and cathodic time of 10 ms had the poorest corrosion stability, for both investigated average deposition current density. Among all investigated alloy coatings the highest corrosion stability was obtained for Zn-Co alloy coatings deposited with pulsed current at higher average current density (jav = 4 A dm-2)., Ispitivano je elektrohemijsko taloženje cink-kobalt legure pulsirajućom strujom na čeliku, a s ciljem dobijanja zaštitnih prevlaka sa povećanom korozionom stabilnošću. Prevlake legura su taložene pulsirajućim režimom sa različitim srednjim gustinama struje i pri različitom trajanju katodnog pulsa. Analiziran je uticaj ovih parametara na iskorišćenje struje prilikom elektrohemijskog taloženja na izgled prevlaka (snimanje elektronskim mikroskopom), hrapavost prevlaka i njihovu korozionu stabilnost u 3% NaCl (merenjem slobodnog korozionog potencijala u agensu korozije i snimanjem polarizacionih krivih). Pokazano je da u zavisnosti od vremena pulsa, prevlake taložene pulsirajućim režimom mogu da imaju bolju homogenost, sitnije aglomerate kristalnih zrna i manju hrapavost od onih taloženih pri istim uslovima, ali konstantnom gustinom struje. Veću korozionu stabilnost pokazale su prevlake legura taložene većom srednjom gustinom struje.", publisher = "Association of Chemical Engineers of Serbia", journal = "Hemijska industrija", title = "The study of Zn-Co alloy coatings electrochemically deposited by pulse current, Ispitivanje prevlaka Zn-Co legura dobijenih pulsirajućom strujom", volume = "66", number = "5", pages = "749-757", doi = "10.2298/HEMIND111215035B" }
Bajat, J., Maksimović, M. D., Tomić, M. V.,& Pavlović, M.. (2012). The study of Zn-Co alloy coatings electrochemically deposited by pulse current. in Hemijska industrija Association of Chemical Engineers of Serbia., 66(5), 749-757. https://doi.org/10.2298/HEMIND111215035B
Bajat J, Maksimović MD, Tomić MV, Pavlović M. The study of Zn-Co alloy coatings electrochemically deposited by pulse current. in Hemijska industrija. 2012;66(5):749-757. doi:10.2298/HEMIND111215035B .
Bajat, Jelena, Maksimović, Miodrag D., Tomić, Milorad V., Pavlović, Miomir, "The study of Zn-Co alloy coatings electrochemically deposited by pulse current" in Hemijska industrija, 66, no. 5 (2012):749-757, https://doi.org/10.2298/HEMIND111215035B . .